涂炭铝箔在石墨磷酸铁锂电池中的应用研究
摘要：摘要本文分别以普通铝箔（AF）和涂碳铝箔（CCAF）作为正极集流体，制作成9 Ah软包石墨/磷酸铁锂电池（C/LiFePO4），并采用多种测试手段研究和对比了各电池的电化学性能。研究结果显示，采用涂碳铝箔可增大活性物质与集流体间的接触面积，提高电导率，有效降低电池极化。CCAF电池的电化学性能优于AF电池，具体表现为：交流内阻（ACR）降低了7.30 mΩ，相同荷电状态（SOC）下的直流内阻（DCR）降低了9 ~ 12 mΩ，放电平台电压提高了40 mV，瞬间电压反弹速率（dV/dt）降低了0.94 V/h，−20℃的1 C放电效率提高了2.4%，5 C放电容量与 1 C放电容量的比率提高了10.6%，5 C放电温升降低了15.2℃，5 C循环500周容量保持率提高了7.06%。
Abstract:：The electrochemical performances of pouch type 9 Ah lithium iron phosphate/graphite (C/LiFePO4) batteries fabricated with conventional aluminum foil (AF) and carbon coated aluminum foil (CCAF) cathode current collector were studied and compared. Results show that the CCAF current collector could increase the interaction area of active materials with current collector, which improves the overall electrical conductivity and reduces battery resistance and polarization. The electrochemical performance of the batteries fabricated by CCAF is superior to that of AF, and results show as follows: the alter-nating current resistance (ACR) reduced by 7.30 mΩ, the direct current resistance decreased by 9 ~ 12 mΩ under the same state of charge (SOC) condition, the plateau voltage increased by 40 mV and the instant voltage relaxation rate (dV/dt) decreased by 0.94 V/h, the capacity retention increased by 2.4% under 1 C at −20oC, ratio of 5 C discharge capacity to 1 C discharge capacity enhanced by 10.6%, the discharge temperature decreased by 15.2oC at 5 C high-rate, and the capacity retention after 500 circles at 5 C increased by 7.06%.
中文标题：涂炭铝箔在石墨磷酸铁锂电池中的应用研究
英文标题：Investigation on Graphite/LiFePO4 Batteries Fabircated by Carbon-Coated Aluminum Foil Current Collector
发表时间：2017-02-17
作者：
陈 鹏，任 宁，姬学敏，常林荣，邓吉阳，苏 锋，李洪涛
作者简介：
陈 鹏（1988-），男，硕士，工程师，主要从事锂离子电池制作工艺优化与材料研究。
关键词：涂碳铝箔,电化学阻抗,倍率性能,循环性能,磷酸铁锂（LiFePO4）,
Key words：arbon coated aluminum foil,electrochemical impedance,rate performance,cycle performance,lithium iron phosphate (LiFePO4),