文档名：Mg2 、Al3 对制备半水硫酸钙晶须形貌和尺寸的影响
摘要：以二水硫酸钙为原料,通过水热法制备半水硫酸钙晶须,在探究反应温度、反应时间对晶须形貌和尺寸影响基础上,分别系统考察了Mg2+、Al3+浓度对其形貌和尺寸的影响.实验结果表明:在料浆质量分数为2%、反应温度为160℃、反应时间为6h条件下制备的产物其平均长度为273.4μm,平均长径比达到30.4,晶须的形貌为针状且较为均一.在低浓度的Mg2+存在下,半水硫酸钙晶须的直径小,长径比高;Al3+对半水硫酸钙晶须沿c轴的生长有较强的抑制作用,得到的晶须呈现棒状或者纺锤体状.
Abstract：Usingcalciumsulfatedihydrateasrawmaterial,ahydrothermalmethodwasemployedtopreparecalciumsulfatehemihydratewhiskers.Basedonaninvestigationontheeffectsofreactiontemperatureandtimeonthemorphologyandsizeofthewhiskers,asystematicstudywasconductedontheeffectsofMg2+andAl3+concentrationsonthemorphologyandsizeofthewhiskers.Theexperimentalresultsshowedthatundertheconditionsofslurrymassfractionof2%,reactiontemperatureof160℃,andreactiontimeof6h,theaveragelengthoftheproductpreparedwas273.4μm,andtheaveragelength-to-diameterratioreached30.4.Thewhiskerswereneedle-shapedandrelativelyuniform.InthepresenceoflowconcentrationsofMg2+,thediameterofthewhiskerswassmallerandthelength-to-diameterratiowashigher.Al3+hadastronginhibitoryeffectonthegrowthofcalciumsulfatehemihydratewhiskersalongthecaxis,resultinginthatwhiskerswererod-shapedorspindle-shaped.
作者：郭静静 薛甜 程萌 蒲梦林 李雪礼 张琰图Author：GUOJingjing XUETian CHENGMeng PUMenglin LIXueli ZHANGYantu
作者单位：陕西省化学反应工程重点实验室,延安大学化学与化工学院,陕西延安716000
刊名：当代化工 ISTIC
Journal：ContemporaryChemicalIndustry
年，卷(期)：2024, 53(4)
分类号：TQ132.32
关键词：半水硫酸钙 晶须 水热法 长径比
Keywords：Calciumsulfatehemihydrate Whiskers Hydrothermalmethod Lengthtodiameterratio
机标分类号：TD853.34TQ116.21X703.1
在线出版日期：2024年5月17日
基金项目：国家重点研发计划Mg2+、Al3+对制备半水硫酸钙晶须形貌和尺寸的影响[
期刊论文] 当代化工--2024, 53(4)郭静静 薛甜 程萌 蒲梦林 李雪礼 张琰图以二水硫酸钙为原料,通过水热法制备半水硫酸钙晶须,在探究反应温度、反应时间对晶须形貌和尺寸影响基础上,分别系统考察了Mg2+、Al3+浓度对其形貌和尺寸的影响.实验结果表明:在料浆质量分数为2%、反应温度为160℃、反应时间...参考文献和引证文献
参考文献
引证文献
本文读者也读过
相似文献
相关博文
Mg2+、Al3+对制备半水硫酸钙晶须形貌和尺寸的影响 Effect of Mg2+ and Al3+ on Morphology and Size of Prepared Hemihydrate Calcium Sulfate Whiskers
Mg2+、Al3+对制备半水硫酸钙晶须形貌和尺寸的影响.pdf
|