文档名：TP321焊接过程产生层间结晶裂纹和表面液化裂纹的原因和预防措施
摘要：加氢装置因为高温、高压、临氢的特殊环境,使加热炉进出口、反应器进出口、高压换热器进出口管线不得不选用TP321或者TP347材质.但在装置建设过程中,工期紧、焊接环境差、焊工水平层次不齐、焊材成分和可焊接操作性差、对热输入和层间温度控制较苛刻等原因,使得在焊接过程中出现热裂纹等焊接质量问题.为保证TP321材质管道焊接质量,对产生以上质量问题原因进行简要阐述,保证焊接过程合适的热输入、应用合格焊材、保证焊缝组织铁素体含量,从而保证装置试压、开停工过程的安全与稳定性.
Abstract：Duetothespecialenvironmentofhightemperature,highpressureandhydrogeninhydrogenationunit,thepipelinesattheinletandoutletoftheheater,reactorandhigh-pressureheatexchangerhavetobemadeofTP321orTP347.However,intheprocessofdeviceconstruction,duetotightconstructionperiod,poorweldingenvironment,unevenlevelofwelders,poorweldingmaterialcompositionandweldability,andharshcontrolofheatinputandinterlayertemperature,weldingqualityproblemssuchashotcracksoccurintheweldingprocess.InordertoensuretheweldingqualityofTP321pipes,thecausesoftheabovequalityproblemswerebrieflydescribedtoensureproperheatinputduringtheweldingprocess,theapplicationofqualifiedweldingmaterials,andtheferritecontentoftheweldstructure,soastoensurethesafetyandstabilityofthepressuretest,startupandshutdownprocessofthedevice.
作者：王龙己 吴波 赖朝喜Author：WANGLongji WUBo LAIChaoxi
作者单位：浙江石油化工有限公司炼油芳烃事业部,浙江舟山316000
刊名：当代化工
Journal：ContemporaryChemicalIndustry
年，卷(期)：2024, 53(2)
分类号：TG457.6
关键词：加氢装置 TP321 层间结晶裂纹 表面液化裂纹 铁素体 低温共晶体
Keywords：Hydrogenationdevice TP321 Interlayercrystallizationcracks Surfaceliquefactioncracks Ferrite Lowtemperaturecocrystal
机标分类号：TG401TQ050TG111.91
在线出版日期：2024年4月12日
基金项目：TP321焊接过程产生层间结晶裂纹和表面液化裂纹的原因和预防措施[
期刊论文] 当代化工--2024, 53(2)王龙己 吴波 赖朝喜加氢装置因为高温、高压、临氢的特殊环境,使加热炉进出口、反应器进出口、高压换热器进出口管线不得不选用TP321或者TP347材质.但在装置建设过程中,工期紧、焊接环境差、焊工水平层次不齐、焊材成分和可焊接操作性差、对热输...参考文献和引证文献
参考文献
引证文献
本文读者也读过
相似文献
相关博文
TP321焊接过程产生层间结晶裂纹和表面液化裂纹的原因和预防措施 Causes and Preventive Measures of Interlayer Crystallization Cracks and Surface Liquefaction Cracks During TP321 Welding Process
TP321焊接过程产生层间结晶裂纹和表面液化裂纹的原因和预防措施.pdf
- 文件大小:
- 3.16 MB
- 下载次数:
- 60
-
高速下载
|
|