文档名：ZL101铸铝合金在不同振幅下的超声空蚀行为
摘要：利用超声振动空蚀装置研究了ZL101铸铝合金在60,70,80μm振幅下的超声空蚀行为.结果表明:ZL101铸铝合金主要由Al相及少量的Fe、Al0.5Fe3Si0.5相组成,在空泡的反复冲击和溃灭作用下,晶粒内部较软的Al相率先发生空蚀破坏,进而损失晶粒边界,产生小空蚀坑;在不同振幅下,空蚀表面均产生明显的塑性变形和脆性断裂,同时具有明显的打孔和掏空行为;振幅的增大导致超声波强度和最大声压增大,进而导致空蚀环境中的压力波动变大,空泡溃灭增多,ZL101铸铝合金受到的空蚀破坏加剧,空蚀质量损失量增大,蚀坑深度增大.
Abstract：TheultrasoniccavitationbehaviorofZL101castaluminumalloyatamplitudesof60,70and80μmwasstudiedbyultrasonicvibrationcavitationdevice.TheresultsshowthatZL101castaluminumalloywasmainlycomposedofAlphaseandasmallamountofFeandAl0.5Fe3Si0.5phases.Undertherepeatedimpactandcollapseofcavitation,thesofterAlphaseinsidethegrainwasfirstdestroyedbycavitationerosion.Inturn,thegrainboundarieswerelosttoproducesmallcavitationpits.Underdifferentamplitudes,thecavitationsurfaceproducedobviousplasticdeformationandbrittlefracture,andhadobviouspunchingandhollowingbehaviors.Theincreaseoftheamplitudeledtotheincreaseoftheultrasonicintensityandthemaximumsoundpressure,whichinturnledtotheincreaseofthepressurefluctuationinthecavitationenvironmentandtheincreaseofcavitationcollapse,whichintensifiedthecavitationdamageoftheZL101castaluminumalloyandincreasedthecavitationqualitylossandthepitdepth.
作者：崔艳雨 李瑶治 丁清苗 成斌 梁继承 Author：CUIYanyu LIYaozhi DINGQingmiao CHENGBin LIANGJicheng
作者单位：中国民航大学航空工程学院,天津300300中国民航大学交通科学与工程学院,天津300300中国石油天然气股份有限公司天然气销售辽宁分公司,沈阳110000
刊名：腐蚀与防护 ISTICPKU
Journal：CorrosionandProtection
年，卷(期)：2024, 45(6)
分类号：TG172.9
关键词：超声空蚀 振幅 ZL101铸铝合金 空蚀质量损失 表面形貌
Keywords：ultrasoniccavitation amplitude ZL101castaluminumalloy cavitationmassloss surfacemorphology
机标分类号：TG174S834.3+2F279.246
在线出版日期：2024年7月18日
基金项目：民航安全能力建设项目，中国民航大学大学生创新创业项目ZL101铸铝合金在不同振幅下的超声空蚀行为[
期刊论文] 腐蚀与防护--2024, 45(6)崔艳雨 李瑶治 丁清苗 成斌 梁继承利用超声振动空蚀装置研究了ZL101铸铝合金在60,70,80μm振幅下的超声空蚀行为.结果表明:ZL101铸铝合金主要由Al相及少量的Fe、Al0.5Fe3Si0.5相组成,在空泡的反复冲击和溃灭作用下,晶粒内部较软的Al相率先发生空蚀破...参考文献和引证文献
参考文献
引证文献
本文读者也读过
相似文献
相关博文
ZL101铸铝合金在不同振幅下的超声空蚀行为 Ultrasonic Cavitation Behavior of ZL101 Cast Aluminum Alloy at Different Amplitudes
ZL101铸铝合金在不同振幅下的超声空蚀行为.pdf
|