文档名：凹凸棒石增强PA6复合线材制备及3D打印研究
摘要：为提高聚酰胺6(PA6)3D打印样件的力学性能,以凹凸棒石(ATP)为增强填料,通过γ-氨丙基三乙氧基硅烷(KH-550)表面改性ATP,采用熔融共混制备PA6/ATP复合材料并通过单螺杆挤出形成3D打印线材,研究了ATP在3D打印过程中的取向行为及其对PA6力学性能的影响,探讨了填料的增强机制.结果表明,适量的ATP能显著提升PA6的力学性能,拉伸强度和杨氏模量分别为73.8MPa和3.11GPa,较纯PA6提升35%和27%,ATP在PA6基体中有序取向.
Abstract：Toimprovethemechanicalpropertiesofpolyamide6(PA6)3Dprintedsamples,KH-550modifiedattapulgite(ATP)wasintroducedintopolyamide6(PA6).PA6/ATPcompositematerialswerepreparedbymeltblending,andthewiresusingfor3Dprintingwereformedbysinglescrewextrusion.TheorientationbehaviorofATPduringthe3DprintingprocessanditsinfluenceonthemechanicalpropertiesofPA6werestudied,andthereinforcementmechanismofthefillerwasdiscussed.TheresultsshowthatanappropriateamountofATPcansignificantlyimprovethemechanicalpropertiesofPA6,thetensilestrengthandYoung'smodulusreach73.8MPaand3.11GPa,respectively,whichare35%and27%higherthanthoseofpurePA6,theorderedorientationofATPinPA6matrixwasobserved.
作者：倪寅栩 文举 高青青 许高杰 刘丰华 Author：NiYinxu WenJu GaoQingqing XuGaojie LiuFenghua
作者单位：宁波大学材料科学与化学工程学院,浙江宁波315211;中国科学院宁波材料技术与工程研究所,浙江宁波315201盱眙县凹土应用技术研发与成果转化中心,江苏盱眙211700中国科学院宁波材料技术与工程研究所,浙江宁波315201
刊名：非金属矿 ISTIC
Journal：Non-MetallicMines
年，卷(期)：2024, 47(3)
分类号：TD985TQ342+.11
关键词：凹凸棒石 熔融沉积成型 聚酰胺6 复合材料
Keywords：attapulgite fuseddepositionmolding polyamide6 compositematerial
机标分类号：TB332TG146.11TQ323.6
在线出版日期：2024年6月7日
基金项目：凹凸棒石增强PA6复合线材制备及3D打印研究[
期刊论文] 非金属矿--2024, 47(3)倪寅栩 文举 高青青 许高杰 刘丰华为提高聚酰胺6(PA6)3D打印样件的力学性能,以凹凸棒石(ATP)为增强填料,通过γ-氨丙基三乙氧基硅烷(KH-550)表面改性ATP,采用熔融共混制备PA6/ATP复合材料并通过单螺杆挤出形成3D打印线材,研究了ATP在3D打印过程中的取向行...参考文献和引证文献
参考文献
引证文献
本文读者也读过
相似文献
相关博文
凹凸棒石增强PA6复合线材制备及3D打印研究 Preparation and 3D Printing of Attapulgite-Reinforced PA6 Composite Filament
凹凸棒石增强PA6复合线材制备及3D打印研究.pdf
- 文件大小:
- 2.35 MB
- 下载次数:
- 60
-
高速下载
|
|