文档名：飞灰和粉煤灰烧结制备微晶玻璃性能研究
摘要：以飞灰和粉煤灰为主要原料,配以适量废玻璃采用等离子体炉熔融后烧结制备微晶玻璃样品.研究了碱度系数和烧结温度对微晶玻璃体积密度、孔隙率、抗弯强度、硬度、耐酸度和耐碱度的影响,考察了微晶玻璃的重金属浸出毒性.得到制备微晶玻璃的最佳工艺条件为:碱度系数0.6,烧结温度1000℃,在此工艺条件下制备的微晶玻璃材料性能满足JC/T2097-2011规定要求,适应于工业和建筑应用.微晶玻璃的重金属浸出毒性远低于GB/T41015-2021和GB5085.3-2007规定的浸出浓度阈值,可满足资源化指标要求.
Abstract：UsingMSWIflyashandcoalflyashasthemainrawmaterialswithappropriateamountofwasteglass,glassceramicswerepreparedbymeltingandsinteringinaplasmafurnace.Theeffectsofalkalinitycoefficientandsinteringtemperatureonthebulkden-sity,porosity,bendingstrength,hardness,acidresistanceandalkaliresistanceofglassceramicswerestudied,andtheleachingtoxicityofheavymetalsinglassceramicswasinvestigated.Theoptimumprocessconditionsforpreparedglassceramicswereobtainedasfollows:thealkalinitycoefficientwas0.6,thesinteringtemperaturewas1000℃.ThepropertiesoftheglassceramicspreparedunderthisprocessconditionsmeettherequirementsofJC/T2097-2011andsuitableforindustrialandarchitecturalapplications.TheleachingtoxicityofheavymetalsinglassceramicsisfarlowerthantheleachingconcentrationthresholdspecifiedinGB/T41015-2021andGB5085.3-2007,whichcanmeettherequirementsofresourceindicators.
作者：张春飞 赵吕菲 Author：ZhangChunfei ZhaoLvfei
作者单位：西安航天源动力工程有限公司,陕西西安710100中能智诚工程设计有限公司,陕西西安715100
刊名：环境科学与管理
Journal：EnvironmentalScienceandManagement
年，卷(期)：2024, 49(2)
分类号：X773
关键词：飞灰 微晶玻璃 碱度 烧结 性能
Keywords：flyash glassceramics alkalinitycoefficient sinteringtemperature performance
机标分类号：TQ171.727X705TU528
在线出版日期：2024年3月22日
基金项目：国家重点研发计划飞灰和粉煤灰烧结制备微晶玻璃性能研究[
期刊论文] 环境科学与管理--2024, 49(2)张春飞 赵吕菲以飞灰和粉煤灰为主要原料,配以适量废玻璃采用等离子体炉熔融后烧结制备微晶玻璃样品.研究了碱度系数和烧结温度对微晶玻璃体积密度、孔隙率、抗弯强度、硬度、耐酸度和耐碱度的影响,考察了微晶玻璃的重金属浸出毒性.得到制...参考文献和引证文献
参考文献
引证文献
本文读者也读过
相似文献
相关博文
飞灰和粉煤灰烧结制备微晶玻璃性能研究 Study on Properties of Glass Ceramics Prepared by Sintering Fly Ash and Coal Fly Ash
飞灰和粉煤灰烧结制备微晶玻璃性能研究.pdf
- 文件大小:
- 716.48 KB
- 下载次数:
- 60
-
高速下载
|
|