文档名：舰用钛合金及铬涂层抗氧化和腐蚀性能研究
摘要：钛合金舰载武器装备长期处于高温及海水飞溅环境,为延长其使用寿命,采用电弧离子镀技术在其表面制备Cr涂层,并研究钛合金及Cr涂层的抗高温氧化和抗盐雾腐蚀性能.结果表明:由于冷热交替作用,650℃循环氧化1h后,在钛合金表面形成的氧化物和基体上产生裂纹,并形成Ti元素氧化物堆积.电弧离子镀的Cr涂层表面平滑完整,仅发生Cr元素氧化,对基体具有保护作用.盐雾腐蚀720h后,钛合金表面发生腐蚀并产生剥落区域,而电弧离子镀制备的Cr涂层无腐蚀剥落区域,具有良好的抗盐雾腐蚀性能.
Abstract：Inordertoprolongtheservicelifeoftitaniumalloyshipboardweaponsandequipmentintheenvironmentofhightemperatureandseawatersplashing,arcionplatingtechnologywasusedtopre-pareCrcoatingonitssurface,andtheresistancetohightemperatureoxidationandsaltspraycorrosionoftitaniumalloyandCrcoatingwasstudied.Theresultsshowthatduetothealternatingeffectofcoldandheat,aftercyclicoxidationat650℃for1h,theoxidesandmatrixonthesurfaceoftitaniumalloycrack,andTioxidesaccumulationisformed.ThesurfaceofthearcionplatingCrcoatingissmoothandcomplete,andonlytheoxidationofCrelementoccurs,whichhasaprotectiveeffectonthematrix.After720hofsaltspraycorrosion,thesurfaceofthetitaniumalloyiscorrodedandthespallingareaisgenerated,whiletheCrcoatingpreparedbyarcionplatinghasnocorrosivespallingareaandhasgoodsaltspraycorrosionresistance.
作者：李建普 卢旭东 李冬冬Author：LiJianpu LuXudong LiDongdong
作者单位：沈阳理工大学装备工程学院,辽宁沈阳110158
刊名：电镀与精饰 ISTICPKU
Journal：Plating&Finishing
年，卷(期)：2024, 46(5)
分类号：TG174.4
关键词：钛合金 Cr涂层 盐雾腐蚀 高温氧化
Keywords：titaniumalloy Crcoating saltspraycorrosion hightemperatureoxidation
机标分类号：TG174.4R285.5TS201.2
在线出版日期：2024年5月16日
基金项目：兵器工业集团十四五创新基金项目舰用钛合金及铬涂层抗氧化和腐蚀性能研究[
期刊论文] 电镀与精饰--2024, 46(5)李建普 卢旭东 李冬冬钛合金舰载武器装备长期处于高温及海水飞溅环境,为延长其使用寿命,采用电弧离子镀技术在其表面制备Cr涂层,并研究钛合金及Cr涂层的抗高温氧化和抗盐雾腐蚀性能.结果表明:由于冷热交替作用,650℃循环氧化1h后,在钛合金表...参考文献和引证文献
参考文献
引证文献
本文读者也读过
相似文献
相关博文
舰用钛合金及铬涂层抗氧化和腐蚀性能研究 Research on oxidation resistance and corrosion resistance of marine titanium alloy and chromium coating
舰用钛合金及铬涂层抗氧化和腐蚀性能研究.pdf
- 文件大小:
- 1.42 MB
- 下载次数:
- 60
-
高速下载
|
|