文档名：牵引销铸钢缺陷的激光熔覆研究
摘要：以牵引销用铸钢(25号钢)为基体,利用激光熔覆技术熔覆奥氏体不锈钢涂层,采用光学显微镜、扫描和透射电镜、X射线衍射仪对熔覆层的组织和结构进行分析和表征,利用显微硬度计和磨损试验机对其硬度和磨损性能进行测试.结果表明:奥氏体不锈钢熔覆层由等轴晶、树枝晶和平面晶组成,热影响区由马氏体和索氏体组成.熔覆层树枝晶内为γ相,树枝晶间由γ相和碳化物Cr3C2构成.显微硬度自熔覆层—热影响区—基体,依次递减为310HV01-280HV0.1-170HV0.1.25号钢基体为黏着磨损和磨料磨损,熔覆层为磨料磨损;磨损1h后熔覆层的耐磨性能是25号钢基体的2倍.
Abstract：Theausteniticstainlesssteelwascoatedon25steeltractionpinbylasercladdingtechnology,andthemicrostructureandstructureofthecoatingwereanalyzedandcharacterizedbyopticalmicroscopy,scan-ningandtransmissionelectronmicroscopyandX-raydiffractometer.Thehardnessandwearpropertiesofthecoatingweretestedbymicrohardnessandweartesters.Theresultsshowthatthecladdinglayeroftheaustenit-icstainlesssteeliscomposedofequiaxed,dendriteandplanarcrystals,andtheheataffectedzoneiscom-posedofmartensiteandsorbite.Theinnerdendriteofthecladdinglayerisγphase,andtheinterdendriteiscomposedofγphaseandcarbideCr3C2.Themicrohardnessofthecladdinglayer,heataffectedzoneandma-trixare310HV0.1,280HV0.1and170HV0.1,respectively.Theweartestindicatesthatthematrixofthesteelisadhesivewearandabrasivewear,andthecladdinglayerisabrasivewear.Thewearresistanceoftheclad-dinglayeristwicethatofthe25steelmatrixafter1hweartest.
作者：刘芳 郭子铭 尚纯 陆兴Author：LIUFang GUOZiming SHANGChun LUXing
作者单位：大连交通大学材料科学与工程学院,辽宁大连116028
刊名：大连交通大学学报
Journal：JournalofDalianJiaotongUniversity
年，卷(期)：2024, 45(1)
分类号：
关键词：激光熔覆 铸钢 显微组织 磨损性能
Keywords：lasercladding caststeel microstructure wearproperty
机标分类号：TG174.44O657.31TF777.1
在线出版日期：2024年4月24日
基金项目：大连市科技创新基金项目牵引销铸钢缺陷的激光熔覆研究[
期刊论文] 大连交通大学学报--2024, 45(1)刘芳 郭子铭 尚纯 陆兴以牵引销用铸钢(25号钢)为基体,利用激光熔覆技术熔覆奥氏体不锈钢涂层,采用光学显微镜、扫描和透射电镜、X射线衍射仪对熔覆层的组织和结构进行分析和表征,利用显微硬度计和磨损试验机对其硬度和磨损性能进行测试.结果表...参考文献和引证文献
参考文献
引证文献
本文读者也读过
相似文献
相关博文
牵引销铸钢缺陷的激光熔覆研究 Study on Laser Cladding Repair of Cast Steel Surface Defect for Traction Pin
牵引销铸钢缺陷的激光熔覆研究.pdf
- 文件大小:
- 3.18 MB
- 下载次数:
- 60
-
高速下载
|
|