文档名：羟乙基纤维素对不同厚度电解铜箔性能的影响
摘要：[目的]研究镀液中羟乙基纤维素(HEC)质量浓度对不同厚度电解铜箔性能的影响.[方法]通过电镀制备了厚度分别为12、18和35μm的电解铜箔.研究了镀液中HEC质量浓度对不同厚度铜箔光泽度、粗糙度、组织结构及力学性能的影响.[结果]HEC质量浓度对35μm铜箔性能和组织结构的影响最大,对12μm铜箔的影响最小.电镀制备12、18和35μm铜箔时,宜将镀液的HEC质量浓度分别控制在5～10mg/L、5～15mg/L和5～10mg/L范围内,以获得力学性能合格的铜箔.[结论]合理控制镀液添加剂浓度有利于获得力学性能优良的电解铜箔.
Abstract：[Introduction]Theeffectofmassconcentrationofhydroxyethylcellulose(HEC)onpropertiesofelectrolyticcopperfoilwithdifferentthicknessneedstobestudied.[Method]Electrolyticcopperfoilswithdifferentthicknesswerepreparedbyelectroplating.TheeffectofmassconcentrationofHEConglossiness,roughness,andmicrostructureatmatteside,andmechanicalpropertiesofcopperfoilswithdifferentthicknesswerestudied.[Result]ThemassconcentrationofHEChadthegreatestimpactonthepropertiesandmicrostructureof35μm-thickcopperfoil,whiletheleastinfluenceonthe12μm-thickcopperfoil's.ItisrecommendedtocontrolthemassconcentrationofHECintherangeof5-10mg/Lfor12μm-thickcopperfoil,5-15mg/Lfor18μm-thickcopperfoil,and5-10mg/Lfor35μm-thickcopperfoilwithqualifiedmechanicalproperties.[Conclusion]Appropriatecontrolofadditivedosageinbathisfavorableforpreparationofelectrolyticcopperfoilswithexcellentmechanicalproperties.
作者：宋言 王阳 Author：SONGYan WANGYang
作者单位：江西铜业技术研究院有限公司,江西南昌330500江西铜业技术研究院有限公司,江西南昌330500;江西电缆有限责任公司,江西吉安343000
刊名：电镀与涂饰
Journal：Electroplating&Finishing
年，卷(期)：2024, 43(4)
分类号：TQ153.1+4
关键词：电解铜箔 羟乙基纤维素 厚度 抗拉强度 断裂伸长率 晶面取向
Keywords：electrolyticcopperfoil hydroxyethylcellulose thickness tensilestrength elongationatbreak crystalplaneorientation
机标分类号：X513TG115.3+13TQ325.14
在线出版日期：2024年5月11日
基金项目：吉安市科技计划羟乙基纤维素对不同厚度电解铜箔性能的影响[
期刊论文] 电镀与涂饰--2024, 43(4)宋言 王阳[目的]研究镀液中羟乙基纤维素(HEC)质量浓度对不同厚度电解铜箔性能的影响.[方法]通过电镀制备了厚度分别为12、18和35μm的电解铜箔.研究了镀液中HEC质量浓度对不同厚度铜箔光泽度、粗糙度、组织结构及力学性能的影响.[结...参考文献和引证文献
参考文献
引证文献
本文读者也读过
相似文献
相关博文
羟乙基纤维素对不同厚度电解铜箔性能的影响 Effect of hydroxyethyl cellulose on properties of electrolytic copper foil with different thickness
羟乙基纤维素对不同厚度电解铜箔性能的影响.pdf
- 文件大小:
- 954.05 KB
- 下载次数:
- 60
-
高速下载
|
|