文档名：锂硫软包电池容量衰减的失效分析
摘要：采用原位与非原位相结合的方法,将锂硫软包电池循环失效的容量损失进行定量化分析,主要包括可逆容量损失和不可逆容量损失.根据表征实验拆分,可逆容量损失主要由电流极化、电解液缺失和电芯极片膨胀导致的容量损失组成,不可逆容量损失主要由负极沉积硫化锂、隔膜黏附多硫化锂和电解液溶解等容量损失组成.通过计算对比,造成锂硫软包电池循环失效的主要因素为锂金属负极的粉化和硫化锂的沉积(约占47％),其次为隔膜黏附多硫化物约25％.可针对造成循环失效的主要因素进行重点改善,提升锂硫电池的循环性能,推动实用化进程.
Abstract：Anin-situandex-situmethodwasusedtoanalysisthecyclicfailurecapacityoflithium-sulfurpouchcellquantificationally,includingreversibleandirreversiblecapacityloss.Reversibleca-pacitylossaremainlycausedbycurrentpolarization,electrolytelossandelectrodeexpansion,whileirreversiblecapacitylossmainlyconsistsoflithiumsulfidedepositiononnegativeelectrode,polysul-fideadhesiononseparatorandelectrolytedissolution,etc.Accordingtocalculationandcomparison,themainfactorscausedcyclefailureoflithium-sulfurpouchcellarelithiumsulfidedepositionandpulverizationoflithiummetalanodeaccountingforabout47％,meanwhilepolysulfideadhesiononseparatoraccountingforabout25％secondly.Therefore,itisnecessarytofocusonanalysisandim-provementofmajorfactors,soastoimprovethecycleperformanceandpracticalprocessoflithium-sulfurbattery.
作者：杨幸遇 张涛 高文超 刘艳侠 Author：YANGXingyu ZHANGTao GAOWenchao LIUYanxia
作者单位：郑州中科新兴产业技术研究院河南省储能材料与过程重点实验室,河南郑州450003郑州中科新兴产业技术研究院河南省储能材料与过程重点实验室,河南郑州450003;中国科学院过程工程研究所离子液体清洁过程国家重点实验室,北京100190
刊名：电源技术 ISTICPKU
Journal：ChineseJournalofPowerSources
年，卷(期)：2024, 48(4)
分类号：TM912.9
关键词：锂硫软包电池 失效分析 容量衰减 量化分解
Keywords：Li-Spouchcell failureanalysis capacityfading quantificationaldecomposition
机标分类号：TM912.9O646TG139.8
在线出版日期：2024年6月11日
基金项目：锂硫软包电池容量衰减的失效分析[
期刊论文] 电源技术--2024, 48(4)杨幸遇 张涛 高文超 刘艳侠采用原位与非原位相结合的方法,将锂硫软包电池循环失效的容量损失进行定量化分析,主要包括可逆容量损失和不可逆容量损失.根据表征实验拆分,可逆容量损失主要由电流极化、电解液缺失和电芯极片膨胀导致的容量损失组成,不...参考文献和引证文献
参考文献
引证文献
本文读者也读过
相似文献
相关博文
锂硫软包电池容量衰减的失效分析 Capacity fading failure analysis of Li-S pouch cell
锂硫软包电池容量衰减的失效分析.pdf
- 文件大小:
- 899.91 KB
- 下载次数:
- 60
-
高速下载
|
|