文档名：一种高倍率磷酸铁锂正极材料前驱体磷酸铁的制备
摘要：磷酸铁的颗粒、形貌对磷酸铁锂的性能起至关重要的作用.现有氨法工艺制备的磷酸铁具有颗粒尺寸大、颗粒分布不均匀的缺点,影响了磷酸铁锂锂离子扩散速度.在现有氨法工艺上进行优化:在浆料中同时加入酸碱调节剂,陈化过程升温保温后得到晶体结构NH4Fe2(OH)(PO4)2·2H2O的碱式磷酸铁铵,干燥煅烧获得高性能无水磷酸铁.所制备的无水磷酸铁具有一次颗粒40～50nm、颗粒分布均匀规则、比表面积12～13m2/g、物料疏松、杂质含量低等特点,采用此种磷酸铁制备的磷酸铁锂倍率性能高,10C放电比容量大于145mAh/g.
Abstract：Theparticleandmorphologyofironphosphateplayanimportantroleintheperformanceoflithiumironphosphate.Theironphosphatepreparedbytheexistingammoniaprocesshasthedis-advantagesoflargeparticlesizeandunevenparticledistribution,whichaffectsthelithiumiondiffu-sionrateoflithiumironphosphatecathodematerials.Theexistingammoniaprocesswasoptimized:anacid-baseregulatorwasaddedtotheslurry,andaftertheagingprocess,thebasicammoniumfer-ricphosphatewithcrystalstructureofNH4Fe2(OH)(PO4)2.2H2Owasobtained,andtheanhydrousironphosphatewithhighperformancewasobtainedbydryingandcalcining.Thepreparedanhy-drousironphosphatehasthecharacteristicsofprimaryparticlesof40-50nm,uniformandregularparticledistribution,specificsurfaceareaof12-13m2/g,loosematerials,lowimpuritycontent.Therateperformanceofthelithiumironphosphatepreparedbythisironphosphateishigh,andthespe-cificdischargecapacityof10Cismorethan145mAh/g.
作者：郭米艳 张伟 李锦 徐善皖 韩洁Author：GUOMiyan ZHANGWei LIJin XUShanwan HANJie
作者单位：湖北虹润高科新材料有限公司,湖北鄂州424300
刊名：电源技术 ISTICPKU
Journal：ChineseJournalofPowerSources
年，卷(期)：2024, 48(4)
分类号：TM912.9
关键词：晶体结构 碱式磷酸铁铵 无水磷酸铁 磷酸铁锂
Keywords：crystalstructure basicammoniumironphosphate anhydrousironphosphate lithiumironphosphate
机标分类号：TM912.9O646TM242
在线出版日期：2024年6月11日
基金项目：一种高倍率磷酸铁锂正极材料前驱体磷酸铁的制备[
期刊论文] 电源技术--2024, 48(4)郭米艳 张伟 李锦 徐善皖 韩洁磷酸铁的颗粒、形貌对磷酸铁锂的性能起至关重要的作用.现有氨法工艺制备的磷酸铁具有颗粒尺寸大、颗粒分布不均匀的缺点,影响了磷酸铁锂锂离子扩散速度.在现有氨法工艺上进行优化:在浆料中同时加入酸碱调节剂,陈化过程升...参考文献和引证文献
参考文献
引证文献
本文读者也读过
相似文献
相关博文
一种高倍率磷酸铁锂正极材料前驱体磷酸铁的制备 Preparation of iron phosphate precursor of high rate lithium iron phosphate cathode material
一种高倍率磷酸铁锂正极材料前驱体磷酸铁的制备.pdf
- 文件大小:
- 1.33 MB
- 下载次数:
- 60
-
高速下载
|
|