文档名：太阳能电池用球形银颗粒的液相法制备研究
摘要：本工作以硝酸银为银前驱体,抗坏血酸为还原剂,结合表面活性剂的作用,制备了平均粒径为(1.88±0.25)μm的球形银颗粒,同时,研究了还原体系中表面活性剂对银颗粒形貌及尺寸分布的影响,结果表明,柠檬酸三钠能够促进片状纳米银的形成.片状纳米银在长链表面活性剂(阿拉伯树胶、聚乙烯吡咯烷酮、聚乙二醇4000的质量比为4∶1∶1)存在时能够发生有序的自组装,得到表面相对光滑、粒径分布均匀的高球形度银颗粒.抗坏血酸的还原能力随着pH值的增加而逐渐增强.此外,本工作将所得银颗粒与有机载体及玻璃粉混合,通过丝网印刷于硅基底上,850℃烧结后,得到电阻率为3.11μΩ·cm的导电厚膜.
Abstract：Sphericalsilverparticleswithanaveragediameterof(1.88±0.25)μmwerepreparedbyachemicalsolutionapproachusingsilvernitrateasprecursorandascorbicacidasreducingagentintheassistanceofseveralsurfactants.Theeffectsofthesurfactantsonthemorphologyandsizedistributionwereinvestigated.Theresultsshowedthattri-sodiumcitratecouldpromotetheformationofsilvernanoflakes.Whenthemassra-tioofArabicgum,polyvinylpyrrolidenoneandpolyethyleneglycol4000was4:1:1,thesilvernanoflakescouldbeself-assembledtomicron-sizedsilverparticleswithsmoothsurfaceanduniformparticlesizedistribution.ThereducingabilityofascorbicacidincreasedwithincreasingpHvalue.Theas-preparedsilverparticlesweremixedwithorganiccarrierandglasspowderstoformapastewhichwasthenscreen-printedonasili-consubstrateandsinteredat850℃toformaconductivethickfilmwitharesistivityof3.11μΩ·cm.
作者：叶慧 沈天成 陈远志 徐进Author：YEHui SHENTiancheng CHENYuanzhi XUJin
作者单位：厦门大学材料学院,福建厦门361000
刊名：材料导报
Journal：MaterialsReports
年，卷(期)：2024, 38(1)
分类号：O643
关键词：银颗粒 协同作用 晶体生长 导电膜
Keywords：silverparticles synergisticeffect crystalgrowth conductivefilm
机标分类号：TM914.4O611.4TB381
在线出版日期：2024年3月19日
基金项目：太阳能电池用球形银颗粒的液相法制备研究[
期刊论文] 材料导报--2024, 38(1)叶慧 沈天成 陈远志 徐进本工作以硝酸银为银前驱体,抗坏血酸为还原剂,结合表面活性剂的作用,制备了平均粒径为(1.88±0.25)μm的球形银颗粒,同时,研究了还原体系中表面活性剂对银颗粒形貌及尺寸分布的影响,结果表明,柠檬酸三钠能够促进片状纳米银...参考文献和引证文献
参考文献
引证文献
本文读者也读过
相似文献
相关博文
太阳能电池用球形银颗粒的液相法制备研究 A Facile Solution Method for the Preparation of Spherical Silver Particles for the Applications of Solar Cells
太阳能电池用球形银颗粒的液相法制备研究.pdf
- 文件大小:
- 4.08 MB
- 下载次数:
- 60
-
高速下载
|
|