文档名：添加剂对粉煤灰合成堇青石陶瓷性能的影响
摘要：选用高铝粉煤灰、镁砂、硅微粉为合成堇青石的主要原料,分别添加1％、2％、3％的ZrO22和1％、2％、3％的CaF2,在100kN的压力下压制成Φ36mm×36mm圆柱状试样,在1300℃下烧结3h,通过检测试样的体积收缩率、体积密度、显气孔率、吸水率、耐压强度以及XRD分析试样成分、SEM观察试样表面形貌,研究添加剂对堇青石性能的影响.结果表明:ZrO2和CaF2的加入降低了堇青石的烧成温度,增大了堇青石的体积密度和耐压强度,提高了堇青石的致密度,并且ZrO2和CaF2的加入促进了高温堇青石的生成,并且晶体结构均匀完整.
Abstract：Highaluminaflyash,magnesiaandsiliconmicropowderwereselectedasthemainrawmaterialsforsynthesisofcordierite.1％,2％,3％ZrO2and1％,2％,3％CaF2wererespectivelyaddedtomakeΦ36mm×36mmcylindricalsampleunderthepressureof100kN,andsinteredat1300℃for3h.Bydetectingthevolumeshrinkageandvolumedensityofthesample,apparentporosity,waterabsorption,compressivestrength,XRDanalysisofsamplecomposition,SEMobservationofsamplesurfacemorphology,effectoftheadditivesoncordieritepropertieswasstudied.TheresultsshowedthattheadditionofZrO2andCaF2decreasedthesinteringtemperatureofcordierite,increasedthevolumedensityandcompressivestrengthofcordierite,andimprovedthedensityofcordierite.Moreover,theadditionofZrO2andCaF2promotedtheformationofhightemperaturecordierite,andthecrystalstructurewasuniformandcomplete.
作者：张婕 魏瑞丽 刘民生 Author：ZHANGJie WEIRui-lin LIUMing-sheng
作者单位：西安建筑科技大学华清学院,陕西西安710043西安建筑科技大学材料与矿资学院,陕西西安710055
刊名：当代化工 ISTIC
Journal：ContemporaryChemicalIndustry
年，卷(期)：2023, 52(10)
分类号：TQ050.4+2
关键词：堇青石陶瓷 高铝粉煤灰 添加剂
Keywords：Cordieriteceramics Highaluminaflyash Additives
机标分类号：TQ174.1TB383O643
在线出版日期：2024年1月23日
基金项目：陕西省教育厅科研项目，陕西省大学生创新创业训练项目添加剂对粉煤灰合成堇青石陶瓷性能的影响[
期刊论文] 当代化工--2023, 52(10)张婕 魏瑞丽 刘民生选用高铝粉煤灰、镁砂、硅微粉为合成堇青石的主要原料,分别添加1％、2％、3％的ZrO22和1％、2％、3％的CaF2,在100kN的压力下压制成Φ36mm×36mm圆柱状试样,在1300℃下烧结3h,通过检测试样的体积收缩率、体积密度、显气孔率、吸水率...参考文献和引证文献
参考文献
引证文献
本文读者也读过
相似文献
相关博文
添加剂对粉煤灰合成堇青石陶瓷性能的影响 Effect of Additives on Properties of Cordierite Ceramics Synthesized From Fly Ash
添加剂对粉煤灰合成堇青石陶瓷性能的影响.pdf
- 文件大小:
- 5.06 MB
- 下载次数:
- 60
-
高速下载
|
|