文档名：铜离子交换锂铝硅抗菌玻璃的制备及性能研究
摘要：厚度为0.55mm的平板锂铝硅玻璃,在KNO3/NaNO3混合熔盐中进行第1步化学钢化(IOX1),以及在KNO3/NaNO3/CuSO4混合熔盐中进行第2步化学钢化(IOX2),可获得强度高、透明度好、抑菌效果优良的铜基抗菌玻璃.研究不同质量分数的CuSO4对锂铝硅玻璃抗菌性能的影响,结果表明,当工艺条件为:第1步离子交换混盐质量比为w(KNO3):w(NaNO3)=50:50、交换4h,第2步离子交换混盐质量比为w(KNO3):w(NaNO3):w(CuSO4)=90:5:5、交换2.5h,可获得表面应力值高于700MPa、在可见光区透过率>90％、抗菌活性值R≥5的优质抗菌玻璃.
Abstract：Copper-baseantibacterialglasswithhighstrength,goodtransparency,andexcellentantibacterialeffectwaspreparedbydipping0.55mmflatlithiumaluminumsilicateglassinamixtureofKNO3/NaNO3moltensaltasthefirststepofchemicaltempering(IOX1)andKNO3/NaNO3/CuSO4mixedmoltensaltasthesecondstepofchemicaltempering(IOX2).TheeffectofdifferentratioofCuSO4ontheantibacterialpropertiesoftheglasswasinvestigated.Theresultsshowedthatthefirststepwastoexchangeinthemixedsaltwithmassratiow(KNO3):w(NaNO3)was50:50bysoakingfor4hours.Inthesecondstep,themassratioofmixedsaltforionexchangew(KNO3):w(NaNO3):w(CuSO4)was90:5:5,andthesoakingtimewas2.5hours.Underthisprocesscondition,theexcellentantibacterialglasswithasurfacestressvaluemorethan700MPa,atransmittanceofover90％inthevisiblelightregionandanantibacterialactivityvalueR≥5canbeobtained.
作者：罗云侠Author：LUOYunxia
作者单位：福建国光新业科技股份有限公司,福州350015
刊名：玻璃搪瓷与眼镜
Journal：GlassEnamel&OphthalmicOptics
年，卷(期)：2024, 52(4)
分类号：TQ173.4
关键词：抗菌 铜离子 离子交换 化学强化
Keywords：antibacterial copperion ionexchanges chemicalstrengthening
机标分类号：TQ426.6TN253O6
在线出版日期：2024年6月19日
基金项目：铜离子交换锂铝硅抗菌玻璃的制备及性能研究[
期刊论文] 玻璃搪瓷与眼镜--2024, 52(4)罗云侠厚度为0.55mm的平板锂铝硅玻璃,在KNO3/NaNO3混合熔盐中进行第1步化学钢化(IOX1),以及在KNO3/NaNO3/CuSO4混合熔盐中进行第2步化学钢化(IOX2),可获得强度高、透明度好、抑菌效果优良的铜基抗菌玻璃.研究不同质量分数的Cu...参考文献和引证文献
参考文献
引证文献
本文读者也读过
相似文献
相关博文
铜离子交换锂铝硅抗菌玻璃的制备及性能研究 Study on Preparation and Performance of Copper Ion Antibacterial Glass
铜离子交换锂铝硅抗菌玻璃的制备及性能研究.pdf
- 文件大小:
- 918.72 KB
- 下载次数:
- 60
-
高速下载
|
|