文档名：应变速率对7065铝合金等温压缩软化机制的影响
摘要：采用等温压缩实验并结合电子背散射衍射手段,研究了应变速率对7065铝合金热变形行为的影响规律.结果表明,随着应变速率由0.001s-1增加到30s-1,合金的动态再结晶面积分数先显著减少,在1s-1时达到较低水平,而后变化幅度小于10％,当应变速率大于1s-1时,合金的亚结构面积分数显著增加.低应变速率阶段(0.001～1s-1)的软化机制为动态再结晶(DRX)机制和动态回复(DRV)机制,而高应变速率阶段(1～30s-1)的软化机制为DRV机制.随着应变速率的增加,等温压缩变形后合金的形变储能逐渐增加.
Abstract：Theeffectofstrainrateonthehotdeformationbehaviorof7065aluminumalloywasinvestigatedbyisothermalcompressionexperimentsandelectronbackscatterdiffraction.Theresultsshowthatasthestrainrateincreasesfrom0.001s-1to30s-1,thedynamicrecrystallizationareafractionofthealloyfirstdecreasessignificantly,reachingalowerlevelat1s-1,andthenthechangeislessthan10％,andthesubstructureareafractionincreasessignificantlywhenthestrainrateisgreaterthan1s-1.Thesofteningmechanismsinthelowstrainraterange(0.001-1s-1)aredynamicrecrystallization(DRX)mechanismanddynamicrecovery(DRV)mechanism,whilethesofteningmechanisminthehighstrainraterange(1-30s-1)isDRV.Withtheincreaseofstrainrate,thedeformationstoredenergyofalloyafterisothermalcompressiondeformationgra-duallyincreases.
作者：赵言 唐建国 张勇 郑许 赵辉 Author：ZHAOYan TANGJianguo ZHANGYong ZHENGXu ZHAOHui
作者单位：中南大学材料科学与工程学院,长沙410083;中南大学有色金属材料科学与工程教育部重点实验室,长沙410083中南大学材料科学与工程学院,长沙410083;中南大学有色金属材料科学与工程教育部重点实验室,长沙410083;广西南南铝加工有限公司铝合金材料与加工重点实验室,南宁530031
刊名：材料导报 ISTICEIPKU
Journal：MaterialsReports
年，卷(期)：2024, 38(8)
分类号：TG146.2
关键词：Al-Zn-Mg-Cu合金 等温压缩 热变形 本构方程 动态再结晶(DRX) 动态回复(DRV)
Keywords：Al-Zn-Mg-Cualloy isothermalcompression hotdeformation constitutiveequation dynamicrecrystallization(DRX) dynamicrecovery(DRV)
机标分类号：TG146.22TG335.11TB333
在线出版日期：2024年6月17日
基金项目：应变速率对7065铝合金等温压缩软化机制的影响[
期刊论文] 材料导报--2024, 38(8)赵言 唐建国 张勇 郑许 赵辉采用等温压缩实验并结合电子背散射衍射手段,研究了应变速率对7065铝合金热变形行为的影响规律.结果表明,随着应变速率由0.001s-1增加到30s-1,合金的动态再结晶面积分数先显著减少,在1s-1时达到较低水平,而后变化幅度...参考文献和引证文献
参考文献
引证文献
本文读者也读过
相似文献
相关博文
应变速率对7065铝合金等温压缩软化机制的影响 Effect of Strain Rate on Isothermal Compression Softening Mechanism of 7065 Aluminum Alloy
应变速率对7065铝合金等温压缩软化机制的影响.pdf
- 文件大小:
- 4.3 MB
- 下载次数:
- 60
-
高速下载
|
|