文档名：稀土尾矿对尾矿陶粒孔结构及性能的影响研究
摘要：为提高稀土尾矿的高值化利用,采用稀土尾矿取代生料制备了尾矿陶粒,探究了稀土尾矿掺量对陶粒孔结构和性能的影响.结果表明,稀土尾矿掺量从0增至40%时,陶粒的堆积密度从1042kg/m3降至495kg/m3,筒压强度从11.7MPa降至2.1MPa;平均孔径从0.24mm增至0.45mm,孔隙率从43.2%增至65.2%;掺入稀土尾矿对陶粒的1h吸水率无明显影响,陶粒的1h吸水率在0.3%～1.3%范围,用稀土尾矿取代生料后的陶粒性能均满足GB/T17431.1-2010要求.
Abstract：Inordertoimprovethehighvalueutilizationofrareearthtailings,thetailingsceramicswerepreparedbyusingrareearthtailingsinsteadofrawmaterials.Theeffectofrareearthtailingscontentontheporestructureandpropertiesofthetailingsceramicswasstudied.Theresultsshowedthatwhenthecontentofrareearthtailingsincreasedfrom0to40%,thebulkdensityofceramsitedecreasedfrom1042kg/m3to495kg/m3,thecylindercompressivestrengthdecreasedfrom11.7MPato2.1MPa.Theaverageporediameterincreasedfrom0.24mmto0.45mm,theporosityincreasedfrom43.2%to65.2%.Theinclusionofrareearthtailingshadnosignificanteffectonthe1hwaterabsorptionofceramsite,whichrangedfrom0.3%to1.3%.Theperformanceofceramsiteafterreplacingrawmaterialswithrare-earthtailingsmettherequirementsofGB/T17431.1-2010.
作者：刘文晟 金超 王宇 陈绍游 蒋俊 Author：LiuWensheng JinChao WangYu ChenShaoyou JiangJun
作者单位：西南科技大学环境友好能源材料国家重点实验室,四川绵阳621010宁波建工工程集团有限公司,浙江宁波315040成都中弘轨道交通股份有限公司,四川成都610095
刊名：非金属矿 ISTIC
Journal：Non-MetallicMines
年，卷(期)：2024, 47(3)
分类号：TD926.4TU523
关键词：稀土尾矿 陶粒 孔结构 性能
Keywords：rareearthtailings ceramsite porestructure property
机标分类号：TU528.062TQ172.44TG174.442
在线出版日期：2024年6月7日
基金项目：宁波市科技计划项目稀土尾矿对尾矿陶粒孔结构及性能的影响研究[
期刊论文] 非金属矿--2024, 47(3)刘文晟 金超 王宇 陈绍游 蒋俊为提高稀土尾矿的高值化利用,采用稀土尾矿取代生料制备了尾矿陶粒,探究了稀土尾矿掺量对陶粒孔结构和性能的影响.结果表明,稀土尾矿掺量从0增至40%时,陶粒的堆积密度从1042kg/m3降至495kg/m3,筒压强度从11.7MPa降至...参考文献和引证文献
参考文献
引证文献
本文读者也读过
相似文献
相关博文
稀土尾矿对尾矿陶粒孔结构及性能的影响研究 Influence of Rare Earth Tailings on the Pore Structure and Properties of Tailings Ceramsite
稀土尾矿对尾矿陶粒孔结构及性能的影响研究.pdf
- 文件大小:
- 1.51 MB
- 下载次数:
- 60
-
高速下载
|
|