文档名：正己胺曼尼希碱缓蚀剂的制备与性能研究
摘要：选取具有苯环结构的苯乙酮和苯甲醛,与正己胺一起制备具有双苯环结构的曼尼希碱缓蚀剂,探索最佳合成条件,拓展正己胺在缓蚀剂领域的开发与应用.通过正交试验与单因素实验,确定最佳合成方案为:醛酮胺摩尔比为0.8∶1∶1,反应温度为85℃,反应时间为7h,介质pH=5.采用静态挂片失重法对制备的曼尼希碱缓蚀剂测试其缓蚀性能.结果表明:当缓蚀剂质量分数为0.5％时,在60℃、20％的盐酸溶液中,对N80钢片的腐蚀速率为1.6207g·(m2·h)-1;当缓蚀剂质量分数为1％时,在90℃、20％的盐酸溶液中,对N80钢片的腐蚀速率为4.7131g·(m2·h)-1,均满足酸化缓蚀剂的指标要求.
Abstract：AcetophenoneandbenzaldehydewithbenzeneringstructurewereselectedtoprepareMannichbasecorrosioninhibitorwithdoublebenzeneringstructuretogetherwithn-hexylamine.Theoptimumsynthesisconditionswereexploredtoexpandthedevelopmentandapplicationofn-hexylamineinthefieldofcorrosioninhibitor.Throughorthogonaltestandsinglefactorexperiment,theoptimumsynthesisschemewasdeterminedasfollows:themolarratioofaldehydetoketonetoaminewas0.8∶1∶1,thereactiontemperaturewas85℃,thereactiontimewas7h,andthemediumpHwas5.ThecorrosioninhibitionperformanceofthepreparedMannichbasecorrosioninhibitorwastestedbystaticweightlossmethod.Theresultsshowthatwhenthemassfractionofcorrosioninhibitoris0.5％,thecorrosionrateofN80steelsheetis1.6207g·(m2·h)-1in20％hydrochloricacidsolutionat60℃.Whenthemassfractionofcorrosioninhibitoris1％,thecorrosionrateofN80steelsheetis4.7131g·(m2·h)-1in20％hydrochloricacidsolutionat90℃,whichmeetstherequirementsofacidificationcorrosioninhibitor.
作者：宋绍富 孙一昊 刘黎晨Author：SONGShao-fu SUNYi-hao LIULi-chen
作者单位：陕西省绿色低碳能源材料与过程工程技术研究中心,陕西西安710065;西安石油大学化学化工学院,陕西西安710065
刊名：当代化工 ISTIC
Journal：ContemporaryChemicalIndustry
年，卷(期)：2023, 52(11)
分类号：TG174.42
关键词：正己胺 曼尼希碱 N80钢片 缓蚀剂
Keywords：N-hexylamine Mannichbase N80steelsheet Corrosioninhibitor
机标分类号：TG174.42TE357O621.3
在线出版日期：2024年1月23日
基金项目：国家自然科学基金正己胺曼尼希碱缓蚀剂的制备与性能研究[
期刊论文] 当代化工--2023, 52(11)宋绍富 孙一昊 刘黎晨选取具有苯环结构的苯乙酮和苯甲醛,与正己胺一起制备具有双苯环结构的曼尼希碱缓蚀剂,探索最佳合成条件,拓展正己胺在缓蚀剂领域的开发与应用.通过正交试验与单因素实验,确定最佳合成方案为:醛酮胺摩尔比为0.8∶1∶1,反应...参考文献和引证文献
参考文献
引证文献
本文读者也读过
相似文献
相关博文
正己胺曼尼希碱缓蚀剂的制备与性能研究 Study on Preparation and Performance of n-Hexylamine MannichBase Corrosion Inhibitor
正己胺曼尼希碱缓蚀剂的制备与性能研究.pdf
- 文件大小:
- 6.36 MB
- 下载次数:
- 60
-
高速下载
|
|