文档名：新型添加剂提高锂电铜箔高温延伸率的研究
摘要：针对目前现有铜箔延伸率较低造成锂电池负极出现断带情况,为解决断带造成电池断路及寿命短的问题,采用生产试验系统制备高延伸率锂电铜箔,主要研究了新型添加剂E-P和E-M对锂电铜箔高温延伸率性能的影响.结果表明,添加剂E-M光亮效果良好,可以作为一种光亮剂来替代常用光亮剂;添加剂E-P或E-M单独作用时,可以一定程度提高延伸率,但作用不明显.然而2种添加剂共同作用时,锂电铜箔的表面形貌更加平整,高温延伸率可提高45%～46%,且表观及其它性能均良好,可以满足客户的要求.
Abstract：Inviewofthecurrentlowelongationoftheexistingcopperfoil,whichcausesthenegativeelectrodeoflithiumbatterytobreak,theproductiontestsystemwasusedtopreparelithiumcopperfoilwithhighelongationinordertosolvetheproblemofbatterybreakandshortservicelifecausedbythebrokentape,andtheeffectofnewadditivesE-PandE-Montheelongationperformanceoflithiumcop-perfoilathightemperaturewasmainlystudied.TheresultsshowthatadditiveE-Mhasgoodbrighten-ingeffectandcanbeusedasasubstituteforcommonbrighteners.AsadditivesE-PorE-Mactalone,theelongationcanbeimprovedtoacertainextent.However,whentheyacttogether,thesurfacemor-phologyoflithiumcopperfoilissmoother,theelongationathightemperaturecanbeincreasedby45%-46%,andtheapparentandotherpropertiesaregood,sothecopperfoilcanmeetcustomers'require-ments.
作者：樊斌锋 王丽娜 王庆福 王江帆Author：FanBinfeng WangLina WangQingfu WangJiangfan
作者单位：河南高精铜箔产业技术研究院有限公司,河南灵宝472500
刊名：电镀与精饰
Journal：Plating&Finishing
年，卷(期)：2024, 46(3)
分类号：TQ153.2
关键词：电解铜箔 锂电铜箔 新型添加剂 高温延伸率
Keywords：electrolyticcopperfoil lithiumcopperfoil newadditives elongationathightemperature
机标分类号：TQ153.1TM912.9TG113.25
在线出版日期：2024年3月22日
基金项目：新型添加剂提高锂电铜箔高温延伸率的研究[
期刊论文] 电镀与精饰--2024, 46(3)樊斌锋 王丽娜 王庆福 王江帆针对目前现有铜箔延伸率较低造成锂电池负极出现断带情况,为解决断带造成电池断路及寿命短的问题,采用生产试验系统制备高延伸率锂电铜箔,主要研究了新型添加剂E-P和E-M对锂电铜箔高温延伸率性能的影响.结果表明,添加剂...参考文献和引证文献
参考文献
引证文献
本文读者也读过
相似文献
相关博文
新型添加剂提高锂电铜箔高温延伸率的研究 Study on improving the elongation of lithium copper foil with new additives at high temperature
新型添加剂提高锂电铜箔高温延伸率的研究.pdf
- 文件大小:
- 1.23 MB
- 下载次数:
- 60
-
高速下载
|
|