文档名：氧化锆的含量和颗粒尺寸对搪玻璃弯曲性能的影响
摘要：搪玻璃化工设备是搪玻璃瓷釉与金属基体经高温熔融形成的复合材料设备,在使用过程中容易产生裂纹导致搪玻璃脱落,影响设备安全运行.通过在搪玻璃瓷釉原料中添加不同含量和直径的氧化锆(ZrO2)颗粒制备搪玻璃试样,研究ZrO2对搪玻璃三点弯曲性能的影响.研究结果表明,添加质量分数为2.2%ZrO2时,搪玻璃板的三点弯曲性能明显提升;ZrO2颗粒平均直径为3μm时,搪玻璃板的三点弯曲性能最好.
Abstract：Glass-linedchemicalequipmentisanirreplaceableproductionequipmentinthepetrochemicalandpharmaceuticalindustries,whichismadeofenamelandmetalmatrixbyhigh-temperaturemelting.Ithasthedualadvantagesofmetalstrengthandglasscorrosionresistanceandeasycleaning.However,cracksarelikelytooccurinservice,causingtheenameltofalloff,affectingthesafeoperationofglass-linedequipment.Tosolvethisproblem,theeffectofzirconiacontentandparticlesizeonfracturetoughnesswasstudiedbyaddingzirconiaduringtheglass-linedsinteringprocess.Theresearchresultsshowedthatthethree-pointbendingperformanceoftheglass-linedboardwassignificantlyimprovedwhenthemassfractionofzirconiaadditionwas2.2wt%,andthethree-pointbendingperformancewasthebestwhenthezirconiaparticleaveragediameterwas3μm.
作者：徐子强 张建军 钟锦林 郭玉 王杰 张梅 李泰来 孙雅宁 徐坤山 Author：XUZiqiang ZHANGJianjun ZHONGJinlin GUOYu WANGJie ZHANGMei LITailai SUNYaning XUKunshan
作者单位：烟台大学化学工程与过程山东省重点实验室,烟台264005潍坊市特种设备检验研究院,潍坊261105淄博市特种设备检验研究院,淄博255035烟台市特种设备检验研究院,烟台265508
刊名：玻璃搪瓷与眼镜
Journal：GlassEnamel&OphthalmicOptics
年，卷(期)：2024, 52(6)
分类号：TQ173.4+8
关键词：搪玻璃 氧化锆 裂纹 韧性 颗粒直径
Keywords：glass-lined ZrO2 cracks toughness particlediameter
机标分类号：TB383TG146.21TQ174
在线出版日期：2024年7月2日
基金项目：山东省自然科学基金，烟台大学实验室开放基金项目氧化锆的含量和颗粒尺寸对搪玻璃弯曲性能的影响[
期刊论文] 玻璃搪瓷与眼镜--2024, 52(6)徐子强 张建军 钟锦林 郭玉 王杰 张梅 李泰来 孙雅宁 徐坤山搪玻璃化工设备是搪玻璃瓷釉与金属基体经高温熔融形成的复合材料设备,在使用过程中容易产生裂纹导致搪玻璃脱落,影响设备安全运行.通过在搪玻璃瓷釉原料中添加不同含量和直径的氧化锆(ZrO2)颗粒制备搪玻璃试样,研究ZrO...参考文献和引证文献
参考文献
引证文献
本文读者也读过
相似文献
相关博文
氧化锆的含量和颗粒尺寸对搪玻璃弯曲性能的影响 The Effect of Zirconia Content and Particle Diameter on Three-point Bending Tests of Glass-lined Enamel
氧化锆的含量和颗粒尺寸对搪玻璃弯曲性能的影响.pdf
- 文件大小:
- 5.92 MB
- 下载次数:
- 60
-
高速下载
|
|