文档名：液固相法合成LiMn0.6Fe0.4PO4的性能
摘要：磷酸锰锂(LiMnPO4)材料的电导率低且充放电过程易发生Jahn-Teller效应,导致电化学性能不理想.通过液-固相法合成磷酸锰铁锂(LiMn0.6Fe0.4PO4)正极材料,并对晶体结构、放电曲线特性、循环性能等进行分析.Fe均匀地掺入Mn位形成固溶体,样品的常温电化学性能得到改善.在2.0～4.3V循环,0.1C倍率下的放电比容量为156.5mAh/g;以1.0C倍率循环2000次,容量保持率超过80％.容量衰减主要源于循环过程中正极材料颗粒产生裂纹及颗粒粉化.
Abstract：Theunidealelectrochemicalperformanceofmanganeselithiumphosphate(LiMnPO4)iscausedbyitslowconductivityandJahn-Tellereffectduringcharge-dischargeprocess.Themanganeseironlithiumphosphate(LiMn0.6Fe0.4PO4)issynthesizedvialiquid-solidphasemethod,itscrystalstructure,dischargecurvecharacteristicandcycleperformanceareanalyzed.TheFeisdopedintotheMnsitetoformsolidsolution,theelectrochemicalperformanceofthesampleatroomtemperatureisimproved.Whencycledin2.0-4.3V,the0.1Cratespecificdischargecapacityis156.5mAh/g,thecapacityretentionrateisabove80％during2000cyclesat1.0Crate.Thecapacityfadingismainlyduetocrackformationandparticlepulverizationofthecathodeduringthecycleprocess.
作者：李亨利 徐荣益 王昭沛 李意能 Author：LIHengli XURongyi WANGZhaopei LIYineng
作者单位：曲靖市德方纳米科技有限公司,云南曲靖655000;佛山市德方纳米科技有限公司,广东佛山528500佛山市德方纳米科技有限公司,广东佛山528500曲靖市德方纳米科技有限公司,云南曲靖655000
刊名：电池 ISTICPKU
Journal：BatteryBimonthly
年，卷(期)：2024, 54(2)
分类号：TM912.9
关键词：锂离子电池 正极材料 磷酸锰铁锂(LiMn0.6Fe0.4PO4) 容量衰减 掺杂 液-固相法 固溶体
Keywords：Li-ionbattery cathodematerial manganeseironlithiumphosphate(LiMn0.6Fe0.4PO4) capacityfading doping liquid-solidphasemethod solidsolution
机标分类号：TM277TM912.9O646
在线出版日期：2024年5月27日
基金项目：云南省科技厅重大科技专项计划项目液-固相法合成LiMn0.6Fe0.4PO4的性能[
期刊论文] 电池--2024, 54(2)李亨利 徐荣益 王昭沛 李意能磷酸锰锂(LiMnPO4)材料的电导率低且充放电过程易发生Jahn-Teller效应,导致电化学性能不理想.通过液-固相法合成磷酸锰铁锂(LiMn0.6Fe0.4PO4)正极材料,并对晶体结构、放电曲线特性、循环性能等进行分析.Fe均匀地掺入Mn位形...参考文献和引证文献
参考文献
引证文献
本文读者也读过
相似文献
相关博文
液-固相法合成LiMn0.6Fe0.4PO4的性能 Performance of LiMn0.6Fe0.4PO4 synthesized via liquid-solid phase method
液-固相法合成LiMn0.6Fe0.4PO4的性能.pdf
- 文件大小:
- 2.14 MB
- 下载次数:
- 60
-
高速下载
|
|