一种结构仿生防污涂料的制备

文档摘要：仿生防污涂料是通过模拟海洋生物的皮肤和结构,或者提取海洋生物体内的防污物质制备出的防污涂料.本文采用简单盐溶解法,通过模拟软珊瑚上层透明层和下层多孔层的复合结构,以不同方式添加软珊瑚体内的防污化学物质糖精、加巴喷丁和正癸酸,制备了组成不同的仿生防污涂料,并对涂料的防污性能进行了研究.研究结果表明,糖精∶加巴喷丁∶正癸酸为47∶23∶25样品的压缩模量最小,糖精∶加巴喷丁∶正癸酸为42∶33∶25样品和糖精含量为0.01g的样品压缩模量次之.压缩模量越小,越容易变形.糖精∶加巴喷丁∶正癸酸为47∶23∶25样品的透明层和多孔层的表面能最小,分别为22.2mJ/m2和16.0mJ/m2.糖精∶加巴喷丁∶正癸酸为42∶33∶25样品和糖精含量为0.01g样品的透明层和多孔层的表面能次之,分别为22.7mJ/m2、22.9mJ/m2和16.1mJ/m2、16.5mJ/m2.表面能越小,疏水性越好,防污性能越好.对样品进行了抗污渍实验和静态抑菌实验,研究表明:和加入单一防污组分的仿生防污涂料相比,将三种防污组分全部加入的仿生防污涂料具有更好的防污效果;加入糖精的样品比加入其它单一防污组分的样品防污效果更好.

Abstract：Thebionicanti-foulingcoatingisananti-foulingcoatingpreparedbysimulatingtheskinandstructureofmarineorganisms,orextractingtheanti-foulingsubstancesinthebodyofmarineorgan-isms.Inthispaper,thesimplesaltdissolutionmethodwasusedtosimulatethecompositestructureoftheuppertransparentlayerandlowerporouslayerofsoftcoral.Theanti-foulingchemicalsubstancesofsaccharin,gabapentinandcapricacidinsoftcoralwereaddedindifferentwaystopreparebionicanti-foulingcoatingswithdifferentcompositions,andthefoulingresistanceofthecoatingswasstudied.Theresultsshowedthatthecompressionmodulusofthesamplewiththeratioofsaccharin∶gabapentin∶cap-ricacidof47∶23∶25wasthesmallest,followedbythesamplewiththeratioof42∶33∶25andthesam-plewith0.01gsaccharin.Thesmallerthecompressionmodulus,theeasieritistodeform.Thesurfaceenergyofthetransparentlayerandporouslayerofthesamplewiththeratioofsaccharin∶gabapentin∶capricacidof47∶23∶25wasthesmallest,whichwas22.2and16.0mJ/m2,respectively.Thesurfaceenergyofthetransparentlayerandporouslayerofthesampleswiththeratioofsaccharin∶gabapentin∶capricacidof42∶33∶25and0.01gsaccharinwassecond,whichwas22.7,22.9and16.1,16.5mJ/m2,respectively.Thesmallerthesurfaceenergy,thebetterthehydrophobicityandanti-foulingperfor-mance.Thesamplesweretestedforstainresistanceandstaticantibacterialexperiments.Theresearchshowedthatcomparedwiththebionicanti-foulingcoatingswithsingleanti-foulingcomponent,thebionicanti-foulingcoatingwithallthreeanti-foulingcomponentshadbetteranti-foulingeffect.Thesamplewithsaccharinhadbetteranti-foulingeffectthanthatwithothersingleanti-foulingcomponents.

作者：高虹  李学田Author：GaoHong  LiXuetian
作者单位：沈阳理工大学环境与化学工程学院,辽宁沈阳110159
刊名：电镀与精饰 ISTICPKU
Journal：Plating&Finishing
年，卷(期)：2024, 46(7)
分类号：TQ152
关键词：仿生  防污涂料  软珊瑚  
Keywords：bionics  antifoulingpaint  softcoral  
机标分类号：TH122TB383R752.1+2
在线出版日期：2024年7月10日
基金项目：一种结构仿生防污涂料的制备[
期刊论文]  电镀与精饰--2024, 46(7)高虹  李学田仿生防污涂料是通过模拟海洋生物的皮肤和结构,或者提取海洋生物体内的防污物质制备出的防污涂料.本文采用简单盐溶解法,通过模拟软珊瑚上层透明层和下层多孔层的复合结构,以不同方式添加软珊瑚体内的防污化学物质糖精、...参考文献和引证文献