文档摘要：低pH值水泥基材料因其低pH值特性被广泛应用于深地质处置库的建设过程中,但其在深地质处置库中的长期服役过程少有研究报道.通过X射线衍射分析、热重分析和扫描电镜等测试,研究了低pH值水泥基材料在深地质处置环境中不同温度下的长期水化产物和微结构演变规律,结果表明:在50℃长期养护下,低pH值水泥基材料的水化产物仍然有钙矾石,可能是由于低pH值水泥基材料的孔隙溶液氢氧根浓度较低,提高了钙矾石的分解温度,导致其在50℃以上仍能长期稳定存在;养护温度越高,低pH值水泥基材料的结合水含量也越高;养护温度的升高,促使箔片状的C-S-H凝胶向细针状的C-S-H凝胶转变.
Abstract：LowpHcementitiousmaterialsarewidelyusedintheconstructionprocessofdeepgeologicaldisposalfacilitiesduetothelowpHcharacteristics,buttherearefewresearchreportsontheirlong-termserviceprocessindeepgeologicaldisposalfacilities.ThehydrationproductsandmicrostructureevolutionoflowpHcementitiousmaterialsatdifferenttemperaturesindeepgeologicaldisposalenvironmentswerestudiedthroughX-raydiffractionanalysis,thermogravimetricanalysis,andscanningelectronmicroscopy.TheresultsshowedthatthehydrationproductsoflowpHcementitiousmaterialsstillcontainettringiteunderlong-termcuringat50℃,whichmaybeduetothelowconcentrationofhydroxideionsintheporesolutionoflowpHcementitiousmaterials,whichincreasesthedecompositiontemperatureofettringiteandleadstoitslong-termstableexistenceabove50℃.Thehigherthecuringtemperature,thehighertheboundwatercontentoflowpHcement-basedmaterials.TheincreaseincuringtemperaturecausesthefoillikeC-S-HgeltotransformintothefineneedlelikeC-S-Hgel.
作者：刘卓霖 李相国 吕阳 Author：LIUZhuolin LIXiangguo LYUYang
作者单位：华南理工大学软物质学院,广州510000;华润水泥技术研发有限公司,广州510000武汉理工大学硅酸盐建筑材料国家重点实验室,武汉430000
刊名：材料导报 ISTICEIPKU
Journal：MaterialsReports
年，卷(期)：2024, 38(z1)
分类号：TU526
关键词：低pH值 养护温度 钙矾石 C-S-H凝胶
Keywords：lowpH curedtemperature Aft C-S-Hgel
机标分类号：TL942.1TG113.12X771
在线出版日期：2024年7月4日
基金项目：养护温度对低pH值水泥基材料水化产物及微结构的影响[
期刊论文] 材料导报--2024, 38(z1)刘卓霖 李相国 吕阳低pH值水泥基材料因其低pH值特性被广泛应用于深地质处置库的建设过程中,但其在深地质处置库中的长期服役过程少有研究报道.通过X射线衍射分析、热重分析和扫描电镜等测试,研究了低pH值水泥基材料在深地质处置环境中不同...参考文献和引证文献