文档摘要：钢筋锈蚀导致横截面积减少,同时锈蚀产物体积膨胀导致混凝土开裂和剥落,影响混凝土与钢筋的粘结能力,对混凝土结构的承载能力和使用寿命产生影响.本文基于国内外广泛的研究成果,分析了不同钢筋锈蚀实验方法的优劣和适用性.对于锈蚀钢筋与混凝土的粘结性能,探讨了中心拉拔试验、偏心拉拔试验和梁式试验的优劣.分别研究了纵筋和箍筋锈蚀对粘结强度的影响,并构建了以钢筋锈蚀率为基础的粘结强度退化模型.锈蚀导致的表面裂缝宽度是评估粘结强度的理想参数,然而基于裂缝宽度的粘结强度退化模型仍然相对较少.在锈蚀钢筋粘结应力-滑移本构模型方面,对未锈蚀和锈蚀钢筋混凝土构件的粘结-滑移关系进行了阐述,然而由于锈蚀钢筋的粘结-滑移曲线测试数据有限,上述模型的可靠性尚未得到验证.本文综述了国内外有关钢筋锈蚀方法和锈蚀钢筋混凝土构件粘结性能的研究方法,分析了纵筋和箍筋锈蚀对粘结强度退化的影响,并归纳总结了基于钢筋锈蚀率和构件表面锈胀裂缝宽度的粘结强度退化模型、以及钢筋混凝土构件粘结-滑移本构关系的最新研究成果.同时,分析了现有研究的不足之处,旨在为未来的钢筋混凝土粘结性能研究提供参考.
Abstract：Thecorrosionofreinforcementinconcretecanleadtoareductionincross-sectionalarea,causingcrackingandspalling.This,inturn,affectsthebondcapacitybetweentheconcreteandreinforcement,ultimatelyimpactingtheload-bearingcapacityandservicelifeofconcretestructures.Thispapercriticallyexaminestheadvantages,disadvantages,andapplicabilityofdifferentexperimentalmethodsusedtostudythecorrosionofreinforcingbars.Theresearchconductedforthisstudyiscomprehensive,encompassingbothdomesticandinternationalsources.Thestudyevaluatesthemeritsanddrawbacksofthreespecifictests:thecenterpullouttest,eccentricpullouttest,andbeamtest.Thesetestsarespecificallyfocusedoninvestigatingthebondpropertiesbetweencorrodedreinforcementandconcrete.Additionally,theeffectsoflongitudinalbarcorrosionandstirrupcorrosiononbondstrengthareanalyzedseparately.Abondstrengthdegradationmodel,whichisestablishedbasedonthecorrosionrateofreinforcement,isalsopresented.Whilethesurfacecrackwidthinducedbycorrosionservesasanidealparameterforevaluatingbondstrength,thereisalackofbondstrengthdegradationmodelsthatutilizecrackwidth.Furthermore,thepaperdescribesthebondstress-slipconstitutivemodelingofcorrodedreinforcement,focusingonthebond-sliprelationshipofuncorrodedandcorrodedreinforcedconcretemembers.However,thereliabilityofthesemodelshasyettobeverifiedduetothelimitedavailabilityoftestdataonbond-slipcurvesofcorrodedreinforcement.Thispaperprovidesacomprehensivesurveyofresearchapproachesfocusedonsteelcorrosionandthebondingperformanceofcorrodedsteelreinforcementinconcretestructures.Itinvestigatestheimpactofcorrosionontheweakeningofbondstrengthinbothlongitudinalandstirrupreinforcement.Additionally,itsummarizesrecentresearchfindings,includingdegradationmodelsforbondstrengthbasedonthecorrosionrateofsteelreinforcementandthewidthofsurfacecorrosion-inducedcracksincomponents.Thepaperalsoexplorestheconstitutiverelationshipofbond-slipinRCstructures.Itcriticallyexaminesthecurrentresearchlimitationsandaimstoofferinsightsforfuturestudiesonthebondingperformanceofreinforcedconcreteinrelationtosteelcorrosion.
作者：黄晋 卢微然 殷成龙 付传清 Author：HUANGJin LUWeiran YINChenglong FUChuanqing
作者单位：浙江树人学院城建学院,杭州310015浙江工业大学土木工程学院,杭州310014
刊名：材料导报 ISTICEIPKU
Journal：MaterialsReports
年，卷(期)：2024, 38(z1)
分类号：TU528
关键词：钢筋锈蚀方法 粘结强度试验方法 粘结强度退化模型 粘结应力-滑移本构关系
Keywords：reinforcementcorrosionmethods bondstrengthtestingmethods bondstrengthdegradationmodel bondstress-slipconstitutiverelationship
机标分类号：TU375G64TU528
在线出版日期：2024年7月4日
基金项目：锈蚀对钢筋与混凝土之间粘结性能影响研究综述[
期刊论文] 材料导报--2024, 38(z1)黄晋 卢微然 殷成龙 付传清钢筋锈蚀导致横截面积减少,同时锈蚀产物体积膨胀导致混凝土开裂和剥落,影响混凝土与钢筋的粘结能力,对混凝土结构的承载能力和使用寿命产生影响.本文基于国内外广泛的研究成果,分析了不同钢筋锈蚀实验方法的优劣和适用...参考文献和引证文献
参考文献
引证文献
本文读者也读过
相似文献
相关博文
关键词：钢筋锈蚀方法,粘结强度试验方法,粘结强度退化模型,粘结应力-滑移本构关系,
|
|
1