文档摘要：采用固相反应法制备NiZn和MnZn铁氧体,球磨后对FeSiAl磁粉进行联合包覆,经过压制成型、退火处理制备FeSiAl复合磁粉心.研究了联合包覆对粉心密度、磁导率和功率损耗的影响;同时对磁粉心磁谱进行测试和拟合,分析两种磁化机制对FeSiAl磁粉心磁导率的贡献.结果表明,采用两种铁氧体联合包覆方案,可以不明显降低复合磁粉心的磁导率,同时降低功率损耗.采用NiZn、MnZn铁氧体均0.5wt%的联合包覆方案,制备的FeSiAl复合磁粉心密度为6.40g/cm3,磁导率为74.4,在50kHz、100mT的测试条件下功率损耗为156.2mW/cm3.NiZn的高电阻率特性能够降低复合磁粉心的涡流损耗;MnZn通过影响畴壁位移和磁畴转动稳定复合磁粉心的磁导率.
Abstract：NiZnandMnZnferriteswerepreparedviaconventionalceramicmethod.ThenbycoatingNiZnandMnZnferritetheFeSiAlmagneticpowdercoreswerepreparedbypressingandsubsequentlyannealingtreatment.TheeffectofcoatingofNiZnandMnZnferriteondensity,permeabilityandpowerlossofFeSiAlpowdercorewerestudied.Thesamples'magneticspectrumwastestedandfitted,tostudytwomagnetizationmechanisms.Theresultsshowthatthemultipleferritejointcoatingcannotsignificantlyreducethepermeabilityofthecompositemagneticcore,andreducethepowerloss.Bycoating0.5wt%ofNiZnandMnZnferrite,FeSiAlmagneticpowdercorewaspreparedfeaturingdensityof6.40g/cm3,permeabilityof74.4andpowerlossof156.2mW/cm3at50kHzand100mT.ThehighresistivityofNiZnferritecanreducetheeddycurrentlossofthemagneticpowdercores.MnZnferritekeepsthepermeabilityofmagneticpowdercoresbyaffectingdomainwalldisplacementanddomainrotation.
作者：陈劼宁 管弦 邬传健 张美蓉 朱圆圆 胡庚 李启帆 孙科 兰中文 余忠 Author：CHENJie-ning GUANXian WUChuan-jian ZHANGMei-rong ZHUYuan-yuan HUGeng LIQi-fan SUNKe LANZhong-wen YUZhong
作者单位：电子科技大学材料与能源学院,四川成都610054深圳市麦捷微电子科技股份有限公司,广东深圳518100
刊名：磁性材料及器件
Journal：JournalofMagneticMaterialsandDevices
年，卷(期)：2024, 55(2)
分类号：TM271+.2
关键词：FeSiAl磁粉心 铁氧体 包覆 磁导率 功率损耗
Keywords：FeSiAlmagneticpowdercores ferrite jointcoating permeability powerloss
机标分类号：TM277TM732TG1
在线出版日期：2024年5月20日
基金项目：软磁铁氧体联合包覆对FeSiAl磁粉心性能的影响[
期刊论文] 磁性材料及器件--2024, 55(2)陈劼宁 管弦 邬传健 张美蓉 朱圆圆 胡庚 李启帆 孙科 兰中文 余忠采用固相反应法制备NiZn和MnZn铁氧体,球磨后对FeSiAl磁粉进行联合包覆,经过压制成型、退火处理制备FeSiAl复合磁粉心.研究了联合包覆对粉心密度、磁导率和功率损耗的影响;同时对磁粉心磁谱进行测试和拟合,分析两种磁化机...参考文献和引证文献