文档摘要：采用手工钨极氩弧焊焊接不同厚度(25mm/18mm)TC4钛合金板(150mm×150mm),对其分别进行去应力退火(600℃/4h)、等温退火(930℃/2h+530℃/4h)并与未热处理(自然冷却)态进行比较,分析不同热处理工艺对焊缝的组织和力学性能的影响.结果表明,未热处理态焊缝区组织为马氏体,去应力退火后组织为较粗大的针状马氏体,等温退火(930℃/2h+530℃/4h)焊缝根部和顶部组织主要为针状马氏体,中部组织则为马氏体+片状α相,此时焊缝的维氏硬度为434HV.由于等温退火后Al含量降低使合金抗拉强度增大,抗拉强度为904MPa,伸长率为8.0%,拉伸断口在母材区域,属于韧性断裂.
Abstract：Themanualargontungsten-arcweldingwasusedtoweldTC4titaniumalloyplate(150mmX150mm)ofdifferentthickness(25mm/18mm).Thestressreliefannealingandisothermalannealingwereimplementedontheplate,thestatusofwhichwascomparedwiththatofnaturalcooling(withoutheattreatment)sample.Theeffectofdifferentheattreatmentprocessonmicrostructureandmechanicalpropertiesofweldareawasanalyzed.Theresultsshowthatmicrostructureofweldareawithoutheattreatmentandthestressreliefannealingaremartensiteandaroughacicularmartensite,respectively.Afterisothermalannealing(930℃/2h+530℃/4h),themicrostructurearemainlyacicularmartensiteatrootandtopoftheweldarea,withmartensite+sliceαphaseatthecentralweldarea,whiletheVickershardnessoftheweldareais434HV.ThetensilestrengthofalloywasincreasedbythelowercontentofAlelementafterisothermalannealing.Tensilestrengthis904MPa,theelongationis8.0%,andthetensilefractureintheregionofthebasemetalbelongstotheductilefracture.
作者：李振亮 李扬 李欣 董瑞 石玉 辛海鹰 Author：LIZhen-liang LIYang LIXin DONGRui SHIYu XINHai-ying
作者单位：内蒙古科技大学材料与冶金学院,内蒙古包头,014010内蒙古科技大学材料与冶金学院,内蒙古包头014010;中国兵器工业第五二研究所,内蒙古包头014030包头市特种设备检验所,内蒙古包头,014030中国兵器工业第五二研究所,内蒙古包头,014030
刊名：内蒙古科技大学学报
Journal：JournalofInnerMongoliaUniversityofScienceandTechnology
年，卷(期)：2017, 36(1)
分类号：TG457.19
关键词：TC4钛合金 钨极氩弧焊 退火 显微组织
机标分类号：
在线出版日期：2017年5月31日
基金项目：内蒙古自然科学基金项目热处理对焊接不等厚TC4钛合金板焊缝微观组织性能影响[
期刊论文] 内蒙古科技大学学报--2017, 36(1)李振亮 李扬 李欣 董瑞 石玉 辛海鹰采用手工钨极氩弧焊焊接不同厚度(25mm/18mm)TC4钛合金板(150mm×150mm),对其分别进行去应力退火(600℃/4h)、等温退火(930℃/2h+530℃/4h)并与未热处理(自然冷却)态进行比较,分析不同热处理工艺对焊缝的组织和力学...参考文献和引证文献