铝合金电镀金鼓包原因分析及解决措施

27 0
1 黄金阳光 发表于 2024-10-4 01:26 | 查看全部 阅读模式
文档摘要:铝合金零件镀金层出现鼓包故障,扫描电镜结果显示鼓包位置有晶间腐蚀形貌,沿晶腐蚀与表面贯通.镍层在局部位置沿晶裂纹渗入到基体内,且在沿晶裂纹内存在P元素.说明沿晶腐蚀在镀镍前已经存在,电镀后晶间腐蚀处被镀层覆盖,因此在结合力检测过程中,在晶间腐蚀产生应力的作用下,该处形成鼓包现象.机械加工和电镀过程中采取一系列防锈措施后,解决了该故障.

Abstract:Thegoldplatinglayerofaluminumalloypartshasbulgingfault,andthescanningelectronmicroscopyresultsshowedthatthelocationofbulginghasintergranularcorrosionmorphology,alongintergranularcorrosionandsurfacepenetration.Thenickellayerinfiltratesintothematrixalongcrystalcracksatlocallocations,andthereisPelementintheintergranularcracks.Thisindicatesthatintergran-ularcorrosionhasalreadyexistedbeforeelectrolessnickelplating,andaftergoldelectroplating,theintergranularcorrosionareaiscoveredbyacoating.Therefore,duringthebindingforcetestingprocess,undertheactionofstressgeneratedbyintergranularcorrosion,bulgingphenomenonisobservedatthislocation.Aftertakingaseriesofrustpreventionmeasuresduringmechanicalprocessingandelectroplating,theproblemissolved.

作者:李大洋  熊俊良Author:LiDayang  XiongJunliang
作者单位:中国空空导弹研究院,河南洛阳471009
刊名:电镀与精饰 ISTICPKU
Journal:Plating&Finishing
年,卷(期):2024, 46(7)
分类号:TQ153.1
关键词:铝合金  镀金  鼓包现象  晶间腐蚀  
Keywords:aluminumalloy  gold-plating  bulgingphenomenon  intergranularcorrosion  
机标分类号:TK229.2TG146.21TQ153.2
在线出版日期:2024年7月10日
基金项目:铝合金电镀金鼓包原因分析及解决措施[
期刊论文]  电镀与精饰--2024, 46(7)李大洋  熊俊良铝合金零件镀金层出现鼓包故障,扫描电镜结果显示鼓包位置有晶间腐蚀形貌,沿晶腐蚀与表面贯通.镍层在局部位置沿晶裂纹渗入到基体内,且在沿晶裂纹内存在P元素.说明沿晶腐蚀在镀镍前已经存在,电镀后晶间腐蚀处被镀层覆盖...参考文献和引证文献
参考文献
引证文献
本文读者也读过
相似文献
相关博文

关键词:铝合金,镀金,鼓包现象,晶间腐蚀,

2024-10-4 01:26 上传
文件大小:
2.52 MB
下载次数:
0
附件售价:
1 下载券 [赞助会员免费下载]
本地下载 立即购买
【温馨提示】 您好!以下是下载说明,请您仔细阅读:
1、推荐使用360安全浏览器访问本站,选择您所需的PDF文档,点击页面下方“本地下载”按钮。
2、耐心等待两秒钟,系统将自动开始下载,本站文件均为高速下载。
3、下载完成后,请查看您浏览器的下载文件夹,找到对应的PDF文件。
4、使用PDF阅读器打开文档,开始阅读学习。
5、使用过程中遇到问题,请联系QQ客服。

本站提供的所有PDF文档、软件、资料等均为网友上传或网络收集,仅供学习和研究使用,不得用于任何商业用途。
本站尊重知识产权,若本站内容侵犯了您的权益,请及时通知我们,我们将尽快予以删除。
  • 手机访问
  • 联系QQ客服
2022-2024 新资汇 - 参考资料分享下载网站
关灯 返回顶部
快速回复 返回顶部 返回列表