文档摘要：采用蔡司金相显微镜、X射线衍射仪、硅钢片磁性能测量仪等对稀土50W470无取向硅钢的组织、织构及磁性能进行了测定.结果表明:稀土50W470无取向硅钢在870,890℃分别以60,70,80m/min连续退火后的显微组织均为再结晶组织,随着退火温度的升高或退火速率的降低,晶粒平均尺寸逐渐变大;退火后,退火织构为Goss织构、{111}织构和{001}织构;890℃退火条件下,随着退火速率的升高,织构因子在退火速率为70m/min时值最小;根据稀土50W470无取向硅钢磁感应强度与铁损的最佳匹配,实验室条件下最佳退火工艺为退火温度890℃,退火速率60m/min.
Abstract：Themicrostructure,textureandmagneticpropertiesofRareEarth50W470non-orientedsiliconsteelweremeasuredbyZEISSmetallographicmicroscope,X-raydiffractometer,siliconsteelsheetmagneticpropertymeasuringinstrument,etc.TheresultsshowthatthemicrostructureofRareEarth50W470nonorientedsiliconsteelisrecrystallizedaftercontinuousannealingat870,890℃atdifferentannealingspeedof60,70and80m/min,respectively.Theaveragegrainsizegraduallyincreaseswiththeincreaseofan-nealingtemperatureorthedecreaseofannealingspeed.Afterannealing,theannealedtextureisGosstexture,{111}textureand{001}texture.Undertheannealingconditionof890℃,withtheincreaseofannealingspeed,thevaluesoftexturefactorarethesmallestwhentheannealingspeedwas70m/min.ToachievethebestmatchbetweenthemagneticinductionstrengthandironlossofRareEarth50W470non-orientedsiliconsteel,thebestannealingprocessunderlaboratoryconditionsisannealingtemperatureof890℃andannealingspeedof60m/min.
作者：李宗维 李涛 韩强 张年迪 孙昭琦 白岩松Author：LIZongwei LITao HANQiang ZHANGNiandi SUNZhaoqi BAIYansong
作者单位：内蒙古科技大学材料与冶金学院,内蒙古包头014010
刊名：内蒙古科技大学学报
Journal：JournalofInnerMongoliaUniversityofScienceandTechnology
年，卷(期)：2023, 42(4)
分类号：TG156.2
关键词：稀土50W470无取向硅钢 连续退火 织构 磁性能
Keywords：rareearth50W470non-orientedsiliconsteel continuousannealing texture magneticproperties
机标分类号：TG156.2TG335.12U465.11
在线出版日期：2024年3月13日
基金项目：国家自然科学基金连续退火工艺对稀土50W470无取向硅钢组织、织构及磁性能的影响[
期刊论文] 内蒙古科技大学学报--2023, 42(4)李宗维 李涛 韩强 张年迪 孙昭琦 白岩松采用蔡司金相显微镜、X射线衍射仪、硅钢片磁性能测量仪等对稀土50W470无取向硅钢的组织、织构及磁性能进行了测定.结果表明:稀土50W470无取向硅钢在870,890℃分别以60,70,80m/min连续退火后的显微组织均为再结晶组织,随...参考文献和引证文献
参考文献
引证文献
本文读者也读过
相似文献
相关博文
关键词：稀土50W470无取向硅钢,连续退火,织构,磁性能,
|
|
1