冷喷涂修复7A01铝合金盐雾腐蚀行为研究

文档摘要：高铁在行驶过程中会受到各种腐蚀介质的腐蚀,使得部件基体损坏,为解决这一问题,采用冷喷涂工艺修复铝合金基体部件.先在7A01铝合金试件中心加工一个凹坑以模拟腐蚀引起的缺陷,随后采用铝基粉末对其冷喷涂修复,最后对修复后的试件进行组织观察、力学性能测定及盐雾腐蚀行为的研究.结果表明:修复后试样凹坑区域气孔和裂纹数量非常少,平均显微硬度为54.5HV,抗拉强度为273.5MPa.经过1000h的中性盐雾实验,冷喷涂修复试样的质量损失率低于未修复的7A01铝合金,修复区域的开路电位高于7A01铝合金.

Abstract：Coldsprayingprocessisusedtorepairthealuminumalloyparts.Forthealuminumalloyspecimenusedintheexperiment,thecenterofthespecimenisfirstmachinedinordertosimulatethedefectscausedbycorrosion,andthenthealuminumbasepowderisrepairedbycoldspraying.Thenthetissueobservation,me-chanicalpropertydeterminationandcorrosionbehavioroftherepairedspecimenarecarriedout.Theresultsshowthatthenumberofporesandcracksintherepairedareaisverysmall,theaveragemicrohardnessoftherepairedareais54.5HV,andthetensilestrengthoftherepairedsampleis273.5MPa.After1000hneutralsaltspraytest,themasslossrateofcoldsprayrepairsampleislowerthanthatof7A01aluminumalloy.Theelectrochemicaltestresultsshowthattheopencircuitpotentialoftherepairregionishigherthanthatof7A01aluminumalloy.Asaresult,therepairedareaprotectsitsnearbysubstratebycorrosionactingasasacrificialanode.Thecorrosionresistanceofthesamplesrepairedbycoldsprayingisbetterthanthatof7A01aluminumalloy.Thecoldsprayingprocessandaluminumbasepowderaresuitablefortherepairofaluminumalloypartsofhigh-speedtrain.

作者：沈长斌  侯明昊  黄诗铭Author：SHENChangbing  HOUMinghao  HUANGShiming
作者单位：大连交通大学材料科学与工程学院,辽宁大连116028
刊名：大连交通大学学报 ISTIC
Journal：JournalofDalianJiaotongUniversity
年，卷(期)：2024, 45(2)
分类号：
关键词：冷喷涂  铝合金  腐蚀性能  
Keywords：coldspray  aluminumalloy  corrosionperformance  
机标分类号：TG174TU528.01TB333
在线出版日期：2024年6月11日
基金项目：辽宁省教育厅基本科研项目，陕西省表面工程与再制造重点实验室天元开放基金项目冷喷涂修复7A01铝合金盐雾腐蚀行为研究[
期刊论文]  大连交通大学学报--2024, 45(2)沈长斌  侯明昊  黄诗铭高铁在行驶过程中会受到各种腐蚀介质的腐蚀,使得部件基体损坏,为解决这一问题,采用冷喷涂工艺修复铝合金基体部件.先在7A01铝合金试件中心加工一个凹坑以模拟腐蚀引起的缺陷,随后采用铝基粉末对其冷喷涂修复,最后对修复...参考文献和引证文献
参考文献
引证文献
本文读者也读过
相似文献
相关博文

关键词：冷喷涂,铝合金,腐蚀性能,

2024-10-4 01:21 上传 冷喷涂修复7A01铝合金盐雾腐蚀行为研究.pdf

文件大小:

1.03 MB

下载次数:

60

高速下载