文档摘要：石墨负极有限的理论容量和倍率性能限制锂离子电池的发展,制备硬碳负极材料可提高理论容量.以间苯二酚和甲醛为前驱体,氨水为催化剂,通过水热法制备酚醛树脂基硬碳材料.采用SEM、高分辨透射电子显微镜(TEM)、XRD及N2吸-脱附对材料的形貌和结构进行分析,并以金属锂片为对电极组装扣式电池,测试电化学性能.硬碳样品具有典型的双电层电容和充放电可逆性,电极以50mA/g电流在0.01～3.00V循环,首次放电比容量达到311.22mAh/g,首次库仑效率为60.07%,循环50次的容量保持率为75.7%,在经过不同电流循环后,基本能恢复到电流变化前的容量,表现出良好的循环稳定性和倍率性能.
Abstract：ThelimitedtheoreticalcapacityandratecapabilityofgraphiteanodelimitthedevelopmentofLi-ionbattery.Thepreparationofhardcarbonanodematerialcanimprovethetheoreticalcapacity.Phenolicresinhardcarbonwithresorcinolandformaldehydeasprecursorsandammoniaascatalystispresentedwithhydrothermalapproach.SEM,high-resolutiontransmissionelectronmicroscopy(TEM),XRDandN2adsorption-desorptionareadoptedtocharacterizethesurfacemorphologyandstructuralfeaturesofthematerials,theelectrochemicalperformanceofthebuttoncellwithlithiummetalascounterelectrodeistested.Thehardcarbonsampleexhibitstypicaldouble-layercapacitanceandreversibilityofchargeanddischarge.Whentheelectrodeiscycledin0.01-3.00Vatacurrentof50mA/g,theinitialspecificdischargecapacityis311.22mAh/gandtheinitialCoulombicefficiencyis60.07%,thespecificcapacityretentionrateis75.7%after50cycles.Aftercyclingatdifferentcurrents,itcanbasicallyreturntothecapacitybeforethecurrentchange,whichpresentsgoodcyclestabilityandratecapacity.
作者：李琼 王治安 朱利民 陈慧 顾秋月Author：LIQiong WANGZhian ZHULimin CHENHui GUQiuyue
作者单位：中国轻工业长沙工程有限公司,湖南长沙410114
刊名：电池 ISTICPKU
Journal：BatteryBimonthly
年，卷(期)：2024, 54(3)
分类号：TM912.9
关键词：锂离子电池 负极材料 硬碳 间苯二酚甲醛树脂 电化学性能
Keywords：Li-ionbattery anodematerial hardcarbon resorcinolformaldehyderesin electrochemicalperformance
机标分类号：TM912.9TM242TB383
在线出版日期：2024年7月17日
基金项目：酚醛树脂基硬碳负极材料的性能[
期刊论文] 电池--2024, 54(3)李琼 王治安 朱利民 陈慧 顾秋月石墨负极有限的理论容量和倍率性能限制锂离子电池的发展,制备硬碳负极材料可提高理论容量.以间苯二酚和甲醛为前驱体,氨水为催化剂,通过水热法制备酚醛树脂基硬碳材料.采用SEM、高分辨透射电子显微镜(TEM)、XRD及N2吸-脱...参考文献和引证文献
参考文献
引证文献
本文读者也读过
相似文献
相关博文
关键词：锂离子电池,负极材料,硬碳,间苯二酚甲醛树脂,电化学性能,
- 文件大小:
- 5.15 MB
- 下载次数:
- 60
-
高速下载
|
|
1