动态人工模拟海水环境下两种B10铜镍合金腐蚀行为

文档摘要：采用动电位极化曲线和电化学阻抗谱测试并结合XPS测试和SEM/EDS微观表征,通过自制的冲刷腐蚀实验装置研究了两种B10铜镍合金在不同流速和不同时间下的冲刷腐蚀行为,比较了两种铜镍合金在不同冲刷条件下的腐蚀差异.结果表明,两种铜镍合金的腐蚀速率随时间的变化规律相似,在不同的流速下冲刷2h后腐蚀速率较高,冲刷8h后腐蚀速率较低.在低于4m/s的流速冲刷不同时间后,A合金的耐蚀性整体上高于B合金的耐蚀性;当流速高于3m/s且较长时间冲刷后,B合金的耐蚀性更好.这与钝化膜中Ni,Fe的化学态无关而与晶粒尺寸和孪晶数量以及Ni,Fe元素的富集有关.长时间高流速冲刷会促进钝化膜中Ni和Fe元素的富集,有利于增强钝化膜的耐蚀性.

Abstract：TheerosioncorrosionbehavioroftwoB10Cu-NialloysinadynamicseawaterenvironmentunderdifferentflowvelocitiesanderosiontimewasinvestigatedbyusingelectrochemicaltechniquesandSEM/EDSinaself-madeexperimentaldeviceforerosioncorrosion.Theresultsdemonstratethatthevariationofthecorrosionrateofthetwoalloyswithtimeissimilar.Thecorrosionrateofthetwoalloysishigheraftertwohoursofimmersionandlowerafterbeingimmersedforeighthoursatdifferentvelocities.ThecorrosionresistanceofalloyAisgenerallyhigherthanthatofalloyBafterbeingimmersedataflowvelocitybelow4m/sfordifferenttime.Whentheflowvelocityishigherthan3m/sandflushingforalongtime,thecorrosionresistanceofalloyBisbetter.Itisrelatedtothegrainsizeandnumberoftwins,aswellastheenrichmentofNiandFe,ratherthanthechemicalstatesofNiandFe.Moreover,NiandFeareenrichedinthepassivationfilmofthetwoalloysafterlong-timeimmersionatahighflowvelocity,whichisbeneficialforenhancingthecorrosionresistanceofthepassivationfilm.

作者：苏英   管勇 Author：SUYing   GUANYong
作者单位：中国科学技术大学材料科学与工程学院,合肥230026;中国科学院金属所,沈阳110016中国科学院金属所,沈阳110016
刊名：材料工程 ISTICEIPKU
Journal：JournalofMaterialsEngineering
年，卷(期)：2024, 52(6)
分类号：TB31
关键词：B10铜镍合金  电化学技术  冲刷腐蚀  钝化膜  腐蚀形貌  
Keywords：B10Cu-Nialloy  electrochemicaltechnique  erosioncorrosion  passivationfilm  corrosionmorphology  
机标分类号：TG172.5TB36TQ153.2
在线出版日期：2024年7月15日
基金项目：动态人工模拟海水环境下两种B10铜镍合金腐蚀行为[
期刊论文]  材料工程--2024, 52(6)苏英  管勇采用动电位极化曲线和电化学阻抗谱测试并结合XPS测试和SEM/EDS微观表征,通过自制的冲刷腐蚀实验装置研究了两种B10铜镍合金在不同流速和不同时间下的冲刷腐蚀行为,比较了两种铜镍合金在不同冲刷条件下的腐蚀差异.结果表...参考文献和引证文献