文档摘要：为提升硫化物的倍率性能和循环稳定性,采用两步电沉积法制备过渡金属硫化物/氢氧化物异质结构复合电极.在碳布上电沉积镍层,改良活性物质与碳布的接触活性;在硫代乙酰胺中添加Zn(NO3)2·7H2O,制备Zn2+掺杂的过渡金属硫化物/氢氧化物异质结构(NCS-Zn-2).NCS-Zn-2在1A/g电流下,比电容达到2703F/g,在150A/g高电流下的比电容是1A/g的40.8%,具有较好的倍率性能.NCS-Zn-2与活性炭组装的工作电压为1.6V高电压水系非对称超级电容器,在794W/kg的比功率下,具有79.9W·h/kg的比能量,以20A/g电流在0～1.6V循环20000次,电容保持率为98.7%.
Abstract：Inordertoimprovetheratecapabilityandcyclingstabilityofsulfides,atwo-stepelectrodepositionmethodisusedtopreparetransitionmetalsulfide/hydroxideheterogeneousstructurecompositeelectrodes.Anickellayeriselectrodepositedonthecarbonclothtoimprovethecontactactivitybetweentheactivesubstanceandthecarboncloth.Zn(NO3)2·7H2OisaddedtothioacetamidetopreparetheZn2+dopedtransitionmetalsulfide/hydroxideheterogeneousstructure(NCS-Zn-2).ThespecificcapacitanceofNCS-Zn-2reaches2703F/gatacurrentof1A/g,andthespecificcapacitanceatahighcurrentof150A/gis40.8%ofthatat1A/g,showinggoodratecapability.AhighvoltageaqueousasymmetricsupercapacitorassembledwithNCS-Zn-2andactivatedcarbonwithanoperatingvoltageof1.6Vhasaspecificenergyof79.9W·h/kgataspecificpowerof794W/kg,thecapacitanceretentionrateis98.7%after20000cyclesin0-1.6Vandacurrentof20A/g.
作者：李涛 柳伟 邵琛琛 李清萍Author：LITao LIUWei SHAOChenchen LIQingping
作者单位：中国海洋大学材料科学与工程学院,山东青岛266100
刊名：电池 ISTICPKU
Journal：BatteryBimonthly
年，卷(期)：2024, 54(3)
分类号：TM533
关键词：超级电容器 Zn2+掺杂 氢氧化物 硫化物 电化学性能
Keywords：supercapacitor Zn2+doping hydroxide sulfide electrochemicalperformance
机标分类号：O646TM912.9TM53
在线出版日期：2024年7月17日
基金项目：山东省自然科学基金重大基础研究项目，山东省省科技计划重点项目Zn2+掺杂硫化物/氢氧化物异质结构的性能[
期刊论文] 电池--2024, 54(3)李涛 柳伟 邵琛琛 李清萍为提升硫化物的倍率性能和循环稳定性,采用两步电沉积法制备过渡金属硫化物/氢氧化物异质结构复合电极.在碳布上电沉积镍层,改良活性物质与碳布的接触活性;在硫代乙酰胺中添加Zn(NO3)2·7H2O,制备Zn2+掺杂的过渡金属硫化...参考文献和引证文献
参考文献
引证文献
本文读者也读过
相似文献
相关博文
关键词：超级电容器,Zn2+掺杂,氢氧化物,硫化物,电化学性能,
|
|
1