文档摘要：以对苯二胺(PPD)和氧化石墨烯(GO)为原料,制备了对苯二胺改性氧化石墨烯(PGO),再通过原位聚合法将苯胺聚合到PGO表面,得到聚苯胺/对苯二胺改性氧化石墨烯(PANI/PGO)复合材料,从而制备PANI/PGO水性环氧树脂防腐涂料.采用扫描电镜(SEM)、红外光谱(FT-IR)和X射线衍射(XRD)对制备的材料进行了表征,利用电化学阻抗谱(EIS)、极化曲线和中性盐雾研究了防腐涂料的防腐性能.结果表明,添加PANI/PGO后环氧树脂涂料展现出更好的防腐性,其涂层获得最大的腐蚀电压Ecorr为-370mV、最小的电流密度Icorr为7.3×10-10A/cm2、最大的极化电阻Rp为8.49×107Ω·cm2.
Abstract：P-phenylenediamine(PPD)andgrapheneoxide(GO)wereusedasrawmaterialstopreparep-phenylenediaminemodifiedgrapheneoxide(PGO).Thenpolyaniline/p-phenylenediaminemodifiedgrapheneox-ide(PANI/PGO)compositematerialwasobtainedthroughpolymerizinganilineonthesurfaceofPGObyin-situpolymerizationmethod.AndfinalPANI/PGOwaterborneepoxyresinanticorrosivecoatingwasprepared.Thepre-paredmaterialwascharacterizedbyscanningelectronmicroscopy(SEM),infraredspectroscopy(FT-IR)andX-raydiffraction(XRD).Theanticorrosivepropertiesofthecoatingswerestudiedbyelectrochemicalimpedancespectroscopy(EIS),polarizationcurveandneutralsaltspraytest.TheresultsshowthattheepoxyresincoatingwithPANI/PGOhasbettercorrosionresistance.ThemaximumcorrosionvoltageEcorris-370mV,theminimumcurrentdensityIcorris7.3×10-10A/cm2,andthemaximumpolarizationresistanceRpis8.49×107Ω·cm2.
作者：曹力文 凌嘉祺 刘薇薇 陈豪杰 王登峰 瞿建刚 Author：CAOLi-wen LINGJia-qi LIUWei-wei CHENHao-jie WANGDeng-feng QUJian-gang
作者单位：南通大学纺织服装学院,江苏南通226019浩力森化学科技(江苏)有限公司,江苏南通226000
刊名：纺织科学与工程学报 ISTIC
Journal：Journaloftextilescience&engineering
年，卷(期)：2024, 41(2)
分类号：TB332
关键词：氧化石墨烯 聚苯胺 防腐 环氧树脂 涂料
Keywords：grapheneoxide polyaniline anticorrosion epoxyresin coating
机标分类号：O627.81TB332TG174.42
在线出版日期：2024年6月27日
基金项目：江苏省产学研合作项目，江苏省研究生科研与实践创新计划项目PANI/PGO水性环氧树脂防腐涂料的制备与性能研究[
期刊论文] 纺织科学与工程学报--2024, 41(2)曹力文 凌嘉祺 刘薇薇 陈豪杰 王登峰 瞿建刚以对苯二胺(PPD)和氧化石墨烯(GO)为原料,制备了对苯二胺改性氧化石墨烯(PGO),再通过原位聚合法将苯胺聚合到PGO表面,得到聚苯胺/对苯二胺改性氧化石墨烯(PANI/PGO)复合材料,从而制备PANI/PGO水性环氧树脂防腐涂料.采用...参考文献和引证文献
参考文献
引证文献
本文读者也读过
相似文献
相关博文
关键词：氧化石墨烯,聚苯胺,防腐,环氧树脂,涂料,