文档摘要：采用传统氧化物烧结工艺制备高介电常数(ε′)钇铁石榴石铁氧体,考察不同烧结温度时Nb5+取代对材料显微结构、晶相、密度(d)、气孔率(p)、晶格常数(a)、饱和磁化强度(4πMs)、铁磁共振线宽(ΔH)和介电常数等磁性能的影响.结果表明,Nb5+取代使材料的晶粒尺寸略微增大;Nb5+取代对材料的晶相无明显影响,均为石榴石纯相;1020℃烧结时,随着Nb5+取代量x由0增大到0.075,4πMs从1882G减小到1741G,ΔH从149.3Oe增大到180.2Oe,烧结体密度从5.83g/cm3减小到5.72g/cm3,烧结体平均晶粒尺寸(D)从2.29μm增加到2.38μm,气孔率(p)从1.7%增大到3.0%,ε′无明显变化.
Abstract：Highdielectricconstant(ε′)yttriumirongarnetferriteswerepreparedbytraditionaloxidesinteringprocess.TheeffectsofNb5+substitutiononthemicrostructure,crystalphase,density(d),porosity(p),latticeconstant(a),saturationmagnetization(4πMs),ferromagneticresonancelinewidth(ΔH)anddielectricconstantofthematerialssinteredatdifferenttemperatureswereinvestigated.TheresultsshowthatNb5+substitutionslightlyincreasesthegrainsizeofthematerial.Nb5+substitutionhasnoobviouseffectonthecrystalphaseofthematerial,whichispuregarnetphase.Whensinteredat1020℃,withtheincreaseofNb5+substitutionamountxfrom0to0.075,4πMsdecreasesfrom1882Gto1741G,ΔHincreasesfrom149.3Oeto180.2Oe,thedensitydecreasesfrom5.83g/cm3to5.72g/cm3,theaveragegrainsize(D)increasesfrom2.29μmto2.38μm,theporosityincreasesfrom1.7％to3.0％,andε′hasnoobviouschange.
作者：胡智勇 余忠 李凌峰 张方远 李启帆 张晓峰 孙科 邬传健 蒋晓娜 兰中文 Author：HUZhi-yong YUZhong LIling-feng ZHANGFang-yuan LIQi-fan ZHANGXiao-feng SUNKe WUChuan-jian JIANGXiao-na LANZhong-wen
作者单位：电子科技大学材料与能源学院,四川成都610054东阳富仕特磁业有限公司,浙江东阳322105
刊名：磁性材料及器件
Journal：JournalofMagneticMaterialsandDevices
年，卷(期)：2024, 55(2)
分类号：TM277+.3
关键词：石榴石铁氧体 Nb5+取代 饱和磁化强度 铁磁共振线宽 介电常数
Keywords：garnetferrite Nb5+substitution saturationmagnetization ferromagneticresonancelinewidth dielectricconstant
机标分类号：TM277TQ123.4TG146.21
在线出版日期：2024年5月20日
基金项目：Nb5+取代对高介电常数钇铁石榴石铁氧体磁性能的影响[
期刊论文] 磁性材料及器件--2024, 55(2)胡智勇 余忠 李凌峰 张方远 李启帆 张晓峰 孙科 邬传健 蒋晓娜 兰中文采用传统氧化物烧结工艺制备高介电常数(ε′)钇铁石榴石铁氧体,考察不同烧结温度时Nb5+取代对材料显微结构、晶相、密度(d)、气孔率(p)、晶格常数(a)、饱和磁化强度(4πMs)、铁磁共振线宽(ΔH)和介电常数等磁性能的影响.结果表明...参考文献和引证文献
参考文献
引证文献
本文读者也读过
相似文献
相关博文
关键词：石榴石铁氧体,Nb5+取代,饱和磁化强度,铁磁共振线宽,介电常数,
- 文件大小:
- 2.31 MB
- 下载次数:
- 60
-
高速下载
|
|
1