文档摘要：为解决乙炔黑单一导电剂自身团聚的问题,采用含碳纳米管(CNT)的导电浆料进行改性.复合后,直径80～100nm的球形乙炔黑颗粒均匀分散在直径20nm的CNT表面,比表面积提高至107.96m2/g.与乙炔黑导电剂电池相比,CNT/乙炔黑电池的电化学阻抗更小、CV曲线面积更大,氧化峰和还原峰的电位差较小(0.19V),以200mA/g在2.75～4.20V循环,首次充放电比容量分别为151.8mAh/g和155.5mAh/g,首次库仑效率为97.6%.第200次循环的放电比容量为141.9mAh/g,容量保持率为92.4%.在5.0C倍率下,CNT/乙炔黑电池的放电比容量为116.9mAh/g,倍率性能更好.
Abstract：Inordertosolvetheproblemofself-agglomerationofacetyleneblacksingleconductiveagent,aconductiveslurrycontainingcarbonnanotubes(CNT)isusedformodification.Aftercompounding,sphericalacetyleneblackparticleswithadiameterof80-100nmareevenlydispersedonthesurfaceofCNTwithadiameterof20nm,thespecificsurfaceareaisincreasedto107.96m2/g.Comparedwithacetyleneblackconductiveagentbattery,CNT/acetyleneblackbatteryhassmallerelectrochemicalimpedanceandlargerCVcurvearea.Thepotentialdifferencebetweentheoxidationpeakandreductionpeakissmaller(0.19V).Whencycledat200mA/gin2.75-4.20V,theinitialcharge/dischargespecificcapacitiesoftheCNT/acetyleneblackbatteryare151.8mAh/gand155.5mAh/grespectively,theinitialCoulombicefficiencyis97.6%.After200cycles,thespecificdischargecapacityofCNT/acetyleneblackbatteryis141.9mAh/g,thecapacityretentionrateis92.4%,thespecificdischargecapacityat5.0Cis116.9mAh/g,theratecapabilityisbetter.
作者：曹米红 张骞 李路成 陈军 Author：CAOMihong ZHANGQian LILucheng CHENJun
作者单位：江西理工大学材料科学与工程学院,江西省动力电池及其材料重点实验室,江西赣州341000江西理工大学材料科学与工程学院,江西省动力电池及其材料重点实验室,江西赣州341000;江西理工大学宜春江理锂电新能源产业研究院,江西宜春336023
刊名：电池 ISTICPKU
Journal：BatteryBimonthly
年，卷(期)：2024, 54(3)
分类号：TM912.9
关键词：锂离子电池 三元正极材料 复合导电剂 乙炔黑 碳纳米管(CNT)
Keywords：Li-ionbattery ternarycathodematerial compositeconductiveagent acetyleneblack carbonnanotubes(CNT)
机标分类号：TM912.9TQ131.11TN304
在线出版日期：2024年7月17日
基金项目：国家自然科学基金，江西省自然科学基金，江西省自然科学基金，江西理工大学清江拔尖人才计划CNT/乙炔黑复合导电剂对LiNi0.5Co0.2Mn0.3O2的影响[
期刊论文] 电池--2024, 54(3)曹米红 张骞 李路成 陈军为解决乙炔黑单一导电剂自身团聚的问题,采用含碳纳米管(CNT)的导电浆料进行改性.复合后,直径80～100nm的球形乙炔黑颗粒均匀分散在直径20nm的CNT表面,比表面积提高至107.96m2/g.与乙炔黑导电剂电池相比,CNT/乙炔黑...参考文献和引证文献
参考文献
引证文献
本文读者也读过
相似文献
相关博文
关键词：锂离子电池,三元正极材料,复合导电剂,乙炔黑,碳纳米管(CNT),
|
|
1